Scientific Reports volume 12, Article number: 14348 (2022) Cite this article

The relatively high cost of all-vanadium redox flow batteries (VRFBs) limits their widespread deployment. Enhancing the kinetics of the electrochemical reactions is needed to increase the power density and energy efficiency of the VRFB, and hence decrease the kWh cost of VRFBs. In this work, hydrothermally synthesized hydrated tungsten oxide (HWO) nanoparticles, C76, and C76/HWO were deposited on carbon cloth electrodes and tested as electrocatalysts for the VO2+/VO2+ redox reactions. Field Emission Scanning Electron Microscopy (FESEM), energy-dispersive X-ray spectroscopy (EDX), high-resolution transmission electron microscope (HR-TEM,), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FTIR), and contact angle measurements were used to characterize the electrodes’ material. The addition of the C76 fullerene to HWO was found to boost the electrode kinetics towards the VO2+/VO2+ redox reaction, by enhancing the conductivity and providing oxygenated functional groups at its surface. A composite of HWO/C76 (50 wt% C76) was found to be the optimum for the VO2+/VO2+ reaction, showing a ΔEp of 176 mV, compared to 365 mV in the case of untreated carbon cloth (UCC). Besides, HWO/C76 composites showed a significant inhibition effect for the parasitic chlorine evolution reaction due to the W-OH functional groups.

The intensive human activities and the rapid industrial revolution have led to unstoppable high demand for electrical energy that increases yearly by about 3%1. The extensive use of fossil fuels as an energy source for several decades resulted in greenhouse gas emissions that have contributed to global warming, water pollution, and air pollution, threatening the entire ecosystem. Therefore, the penetration of clean and renewable wind and solar energies is expected to reach up to 75% of the total electrical energy by 20501. However, the electrical grid becomes unstable when the power from renewable energy sources exceeds 20% of the total generated power1. Developing efficient energy storage systems is crucial for such a transition since they are required to store surplus electricity and balance supply and demand.

Among all energy storage systems such as hybrid vanadium redox flow batteries2, all-vanadium redox flow batteries (VRFBs) are the most developed for their numerous advantages3, and are thought to be an optimal solution for long-term energy storage (~ 30 years) when combined with renewable energy sources4. This is due to the decoupling of power and energy densities, fast response, long cycle life, and relatively low annualized cost of $65/kWh in comparison to $93–$140/kWh and $279–$420/kWh for Li-ion and lead-acid batteries, respectively4.

However, their extensive commercialization is still impeded by their relatively high system capital cost, primarily due to the cell stack4,5. Therefore, improving the cell stack performance by increasing the kinetics of both half-cell reactions can reduce the size of the stack and, consequently, the cost. Therefore, fast electron transfer at the electrode’s surface is needed, which depends on the electrode’s design, composition, and structure that needs to be optimized carefully6. Even though carbon-based electrodes have good chemical and electrochemical stability and good conductivity, with no treatment they suffer from sluggish kinetics due to the lack of oxygen functional groups and hydrophilicity7,8. Therefore, different electrocatalysts were incorporated with the carbon-based electrodes, specifically carbon nanostructures and metal oxides, to enhance the kinetics at both electrodes to increase the kinetics at the VRFB electrodes.

Many carbon materials have been used, such as carbon paper9, carbon nanotubes10,11,12,13, graphene-based nanostructures14,15,16,17, carbon nanofibers18, and other19,20,21,22,23, except the fullerene family. In our previous work on C76, we reported for the first time, the superior electrocatalytic activity of this fullerene towards VO2+/VO2+, showing a 99.5% and 97% decrease in charge transfer resistance in comparison to thermally treated and untreated carbon cloth24. A summary of the carbon materials' catalytic performance towards the VO2+/VO2+ reactions in comparison to C76 is given in Table S1. On the other hand, many metal oxides were used, such as CeO225, ZrO226, MoO327, NiO28, SnO229, Cr2O330 and WO331,32,33,34,35,36,37,38, owing to their enhanced wettability and abundant oxygen functional groups. A summary of the catalytic performance of these metal oxides towards VO2+/VO2+ reactions is given in Table S2. Quite a few papers used WO3 due to its low cost, high stability in acidic media, and high catalytic activity31,32,33,34,35,36,37,38. However, the WO3 showed an insignificant improvement in the kinetics of the positive electrode. To improve the conductivity of WO3, the effect of using the reduced tungsten oxide (W18O49) on the activity of the positive electrode was tested38. The hydrated tungsten oxide (HWO) has never been tested in the VRFB application, despite showing enhanced activity in the supercapacitor application due to faster cation diffusion, compared to the anhydrous WOx39,40. The third generation of vanadium redox flow batteries uses mixed acid electrolyte composed of HCl and H2SO4 to enhance the performance of the batters and increase the solubility and stability of vanadium ions in the electrolyte. However, the parasitic chlorine evolution reaction become one of the drawbacks of the third generation and hence finding a way to suppress the chlorine evaluation reaction became the concern of several research groups41.

Herein, HWO/C76 composites, deposited on carbon cloth electrodes, were tested for the VO2+/VO2+ reaction, aiming at finding a balance between the composites' conductivity and the redox reaction kinetics at the electrode surface, in addition to inhibiting the parasitic chlorine evolution reaction (CER). Hydrated tungsten oxide (HWO) nanoparticles were synthesized via facile hydrothermal methods. Experiments were done in the mixed acid electrolyte (H2SO4/HCl) to imitate the 3rd Generation (G3) VRFB for more practicality and to study the effect of HWO on the chlorine evolution parasitic reaction42.

Vanadium (IV) sulfate oxide hydrate (VOSO4, 99.9%, Alfa-Aeser), sulfuric acid (H2SO4), hydrochloric acid (HCl), dimethylformamide (DMF, Sigma-Aldrich), polyvinylidene fluoride (PVDF, Sigma-Aldrich), sodium tungsten oxide dihydrate (Na2WO4, 99%, Sigma-Aldrich), and ELAT Hydrophilic Plain Carbon Cloth (Fuel Cell Store), were used in this study.

Hydrated tungsten oxide (HWO) was fabricated by a hydrothermal reaction43, in which 2 g of Na2WO4 salt was dissolved in 12 mL H2O, giving a colorless solution, then 12 mL of 2 M HCl was added dropwise, resulting in a pale-yellow suspension. This suspension was placed in a Teflon-lined stainless autoclave in an oven at 180 ºC for 3 h to undergo the hydrothermal reaction. The residue was collected by filtration, washed three times with ethanol and H2O, dried in the oven at 70 ºC for ~ 3 h, and then ground to obtain the grey-blue powder of HWO.

The as-received (untreated) carbon cloth (UCC) electrodes were used as it is or thermally treated in a tube furnace in the air at 450 °C for 10 h at a heating rate of 15 ºC/min to produce treated CC (TCC), as in the previous paper24. UCC and TCC were cut into ~ 1.5 cm width × 7 cm length electrodes. C76, HWO, HWO-10% C76, HWO-30% C76, and HWO-50% C76 suspensions were prepared by adding 20 mg of the active material powder and 10 wt% (~ 2.22 mg) PVDF binder into ~ 1 mL DMF and sonicating for 1 h to enhance homogeneity. 2 mg of C76, HWO, and HWO-C76 composites was subsequently loaded onto an active electrode area of ~ 1.5 cm2 of UCC. All the catalysts were loaded on UCC electrodes and TCC was only used for comparison since it was shown in our previous work that thermal treatment is not necessary24. Casting deposition was achieved by brushing 100 µL of the suspension (2 mg loading) for more homogeneity. All electrodes were then oven-dried at 60 °C overnight. Electrodes were measured before and after to ensure accurate mass loading. To have a definite geometric area (~ 1.5 cm2) and to prevent the vanadium electrolyte from going up the electrode by capillary effect, a thin layer of wax was applied on top of the active material.

Field Emission Scanning Electron Microscopy (FESEM, Zeiss SEM Ultra 60, 5 kV) was used to observe the surface morphology of the HWO. Energy-Dispersive X-ray spectroscopy equipped within the Feii8SEM (EDX, Zeiss Inc.) was used for elemental mapping of HWO-50%C76 on UCC electrodes. A high-resolution transmission electron microscope (HR-TEM, JOEL JEM-2100), operating at an accelerating voltage of 200 kV, was used to provide higher resolution imaging and diffraction ring pattern of HWO particles. Crystallographic Tool Box (CrysTBox) software was used to analyze the diffraction ring pattern of HWO using the ringGUI feature, and the results were compared with the XRD pattern44. The structure and graphitization of UCC and TCC were analyzed by X-ray diffraction (XRD) at a scan rate of 2.4°/min from 5° to 70° with Cu Kα (λ = 1.54060 Å), using Panalytical X-ray diffractometer (model 3600). The crystal structure and phase of HWO were revealed by XRD. PANalytical X’Pert HighScore software was utilized to match the peaks of HWO with the tungsten oxide cards available in the database45. Results for HWO were compared with TEM results. The chemical composition and state of the HWO samples were determined by X-ray photoelectron spectroscopy (XPS, ESCALAB 250Xi, ThermoScientific). CASA-XPS software (v 2.3.15) was used to deconvolute the peaks and data analysis. Fourier transform infrared spectroscopy (FTIR, Perkin Elmer spectrometer using KBr FTIR grade) measurements were carried out to determine the surface functional groups of HWO and HWO-50%C76. Results were compared with XPS results. Contact angle measurements (KRUSS DSA25) were also used to characterize the wettability of the electrodes.

A Biologic SP 300 workstation was employed for all electrochemical measurements. Cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) were used to study the electrode kinetics of the VO2+/VO2+ redox reaction and the effect of the reactant (VOSO4 (VO2+)) diffusion on the reaction rate. A three-electrode cell was used for both techniques with an electrolyte concentration of 0.1 M VOSO4 (V4+) in 1 M H2SO4 + 1 M HCl (mixed acid). All the reported electrochemical data was IR corrected. A saturated calomel electrode (SCE) and a platinum (Pt) coil were used as the reference and counter electrodes, respectively. For CV, scan rates (ν) of 5, 20, and 50 mV/s were applied at a potential window of (0–1) V vs. SCE for VO2+/VO2+ and then corrected to the SHE scale for figures plotting (VSCE = 0.242 V vs VSHE). To investigate the activity retention of the electrodes, repetitive cycling CVs were conducted at ν of 5 mV/s for UCC, TCC, UCC-C76, UCC-HWO, and UCC-HWO-50% C76. For EIS measurements, a frequency range of 0.01–105 Hz with a voltage perturbation of 10 mV at the open-circuit voltage (OCV) was used for the VO2+/VO2+ redox reaction. Each experiment was repeated 2–3 times to ensure consistency of the results. The heterogeneous rate constants (k0) were obtained by Nicholson’s method46,47.

Hydrated tungsten oxide (HWO) was successfully synthesized via the hydrothermal method. The SEM image in Fig. 1a showed the deposited HWO to consist of clusters of nanoparticles with particle sizes in the range of 25–50 nm.

The (a) SEM image and (b) XRD spectrum of HWO with all diffraction planes.

The XRD pattern of the HWO exhibited (001) and (002) peaks at ~ 23.5° and ~ 47.5°, respectively, characteristic of the non-stoichiometric WO2.63 (W32O84) (PDF 077–0810, a = 21.4 Å, b = 17.8 Å, c = 3.8 Å, α = β = γ = 90°) consistent with their apparent blue color (Fig. 1b)48,49. Other peaks at about 20.5°, 27.1°, 28.1°, 30.8°, 35.7°, 36.7°, and 52.7° are allocated to (140), (620), (350), (720), (740), (560) and (970) diffraction planes, of orthorhombic WO2.63, respectively49. Songara et al.43, using the same synthesis method, obtained a white color product, which is related to the existence of WO3(H2O)0.333. However, in this work, a blue-grey color product was obtained due to the different conditions, indicating the coexistence of both the WO3(H2O)0.333 (PDF 087-1203, a = 7.3 Å, b = 12.5 Å, c = 7.7 Å, α = β = γ = 90°) and the reduced form of tungsten oxide. The semi-quantitative analysis done by the X’Pert HighScore software displayed 26% WO3(H2O)0.333: 74% W32O84. Since the W32O84 consists of W6+ and W4+ (1.67:1 of W6+:W4+), the estimated content of W6+ and W4+ are about 72% W6+ and 28% W4+, respectively. SEM image, 1 s core-level XPS spectrum, TEM image, FTIR, and Raman spectra of C76 particles are reported in our previous paper24. According to Kawada et al.50,51, the XRD pattern of C76, after toluene removal, showed monoclinic FCC structure.

The SEM images in Fig. 2a and b show the successful deposition of HWO and HWO-50%C76 on and between the carbon fibers of UCC electrodes. Tungsten, carbon, and oxygen EDX elemental mapping for the SEM image in Fig. 2c that is demonstrated in Fig. 2d–f show that tungsten and carbon are uniformly mixed (showing similar distribution) all over the electrode surface, with the composite being nonuniformly deposited due to the nature of the deposition method.

SEM images of the (a) deposited HWO and (b) HWO-C76 particles. EDX mapping on the HWO-C76 loaded on UCC using the area in image (c) shows the distribution of tungsten (d), carbon (e), and oxygen (f) in the sample.

HR-TEM was employed for high magnification imaging and crystallography information (Fig. 3). The HWO showed a nanocube morphology as can be seen in Fig. 3a and more clearly in Fig. 3b. Zooming onto the nanocubes for selected area diffraction, the lattice structure, and the diffraction planes satisfying Bragg’s law could be visualized as depicted in Fig. 3c, confirming the crystallinity of the material. The inset of Fig. 3c shows a d-spacing of 3.3 Å, corresponding to the (022) and (620) diffraction planes found in WO3(H2O)0.333 and W32O84 phases, respectively43,44,49. This is consistent with the above XRD analysis (Fig. 1b), as the d-spacing of the observed lattice plane (Fig. 3c) corresponds to the most intense XRD peak in the HWO sample. The ring pattern is also displayed in Fig. 3d with each ring corresponding to a different plane. WO3(H2O)0.333 and W32O84 planes are written in white and blue, respectively, with their respective XRD peaks also depicted in Fig. 1b. The first ring shown in the ring pattern corresponds to the first marked peak in the XRD pattern of the diffraction plane (022) or (620). From (022) to (402) rings, the d-spacing values were found to be 3.30, 3.17, 2.38, 1.93, and 1.69 Å, which are consistent with the XRD values of 3.30, 3.17, 2.45, 1.93, and 1.66 Å, respectively44,45.

(a) The HR-TEM image of the HWO, with (b) showing a magnified image. An image of the lattice planes is shown in (c), with the inset of (c) showing a magnified image of the planes and a d-spacing of 0.33 nm, corresponding to (002) and (620) planes. (d) The ring pattern of the HWO, showing the planes associated with WO3(H2O)0.333 (white) and W32O84 (blue) phases.

The XPS analysis was conducted to determine the surface chemistry and oxidation state of tungsten (Figs. S1 and 4). The wide-range XPS scan spectrum of the synthesized HWO is shown in Fig. S1, indicating the presence of tungsten. The XPS narrow scan spectra of W 4f and O 1s core levels are shown in Fig. 4a and b, respectively. The W 4f spectrum was separated into two spin–orbit doublet peaks corresponding to the binding energies of W oxidation states. Whereas the W 4f5/2 and W 4f7/2 peaks located at binding energies of 37.8 and 35.6 eV are ascribed to W6+, the W 4f5/2 and W 4f7/2 peaks at 36.6 and 34.9 eV are characteristic of the W4+ state, respectively 40. The presence of a lower oxidation state (W4+) further confirms the formation of non-stoichiometric WO2.63, while the presence of W6+ indicates stoichiometric WO3 attributed to WO3(H2O)0.333. The fitting data reveal that the atomic percentages of W6+ and W4+ are 85% and 15%, respectively, which are relatively close to the values estimated from the XRD data, taking into consideration the differences between the two techniques. Both techniques give quantitative information with low accuracy, especially XRD. In addition, the two techniques analyze a different portion of materials, as XRD is a bulk technique while XPS is a surface technique that approaches only a few nanometers. The O 1s spectrum was deconvoluted into two peaks at 533 (22.2%) and 530.4 eV (77.8%). The former corresponds to O–H, while the latter is ascribed to the crystal lattice oxygen bond in W–O. The presence of the O–H functional group is consistent with the hydrated nature of HWO.

XPS narrow scan spectrum of (a) W4f. and (b) O1s for the synthesized HWO.

The FTIR analysis was also conducted for these two samples to study the presence of functional groups and the coordinated water molecules in the hydrated HWO structure. The results show that the HWO-50% C76 sample and HWO FT-IR results seem similar due to the presence of HWO, but with different peak intensities due to the different amount of sample that was used during preparation for analysis (Fig. 5a). The HWO-50% C76 show all the peaks reported to fullerene24 in addition to that for the tungsten oxide peaks. In detail, Fig. 5a shows that both samples exhibited very strong broadband at ~ 710/cm assigned to the O–W–O stretch vibration in the HWO lattice structure, an intense shoulder at ~ 840/cm attributed to the W–O stretch vibration, a sharp band at ~ 1610/cm referring to the O–H bending vibration, and a broad absorption band at ~ 3400/cm assigned to the O–H stretch vibration in hydroxyl groups43. These results are consistent with the XPS spectra in Fig. 4b, where W–O functional groups could provide active sites for the VO2+/VO2+ reaction.

FTIR analysis (a) of HWO and HWO-50% C76, indicating the functional groups, and the contact angle measurements (b, c).

The O–H groups could also catalyze the VO2+/VO2+ reaction, along with increasing the hydrophilicity of the electrode, hence facilitating diffusion and electron transfer rate. The HWO-50% C76 sample exhibited additional peaks for C76, as marked on the graph. The peaks at ~ 2905, 2375, 1705, 1607, and 1445/cm could be assigned to C–H, O=C=O, C=O, C=C, and C–O stretching vibrations, respectively14. As already known, C=O and C–O oxygen functional groups could act as active sites for vanadium redox reactions. To test and compare the wettability of both electrodes, contact angle measurements were employed as shown in Fig. 5b, c. The HWO electrode immediately absorbed the water droplet, indicating super hydrophilicity because of the available O–H functional groups. The HWO-50% C76 was more hydrophobic with a contact angle of ~ 135° after 10 s. However, in the electrochemical measurements, the HWO-50% C76 electrode became completely wet in less than a minute. The wettability measurements are consistent with the XPS and FTIR results that showed the more abundant O–H groups on the surface of HWO made it relatively more hydrophilic.

HWO and HWO-C76 nanocomposites were tested for the VO2+/VO2+ reaction, with the anticipation that HWO would inhibit the chlorine evolution that takes place during the VO2+/VO2+ reaction in mixed acid and the C76 to further catalyze the desired VO2+/VO2+ redox reaction. HWO suspensions with 10%, 30%, and 50% C76 were prepared and deposited on UCC electrodes with a total loading of ~ 2 mg/cm2.

The reaction kinetics of VO2+/VO2+ at the electrode surface was examined using CV in the mixed acid electrolyte as shown in Fig. 6. The currents were displayed as I/Ipa to make an easier comparison of the ΔEp and the Ipa/Ipc between the different catalysts directly from the figure. The current per area data is shown in Fig. 2S. Figure 6a shows that the HWO slightly enhances the electron transfer rate of the VO2+/VO2+ redox reaction at the electrode surface and inhibits the parasitic chlorine evolution reaction. While C76 significantly enhances the electron transfer rate and catalyzes the chlorine evolution reaction. Therefore, a composite of the HWO and C76 with the right composition is expected to have the best activity and the highest ability to suppress the chlorine evolution reaction. Upon increasing the C76 content, the electrochemical activity of the electrode was found to improve, as indicated by the reduced ΔEp and increased Ipa/Ipc ratio (Table S3). This was also confirmed by the RCT values (Table S3) extracted from the Nyquist plot in Fig. 6d, which were found to decrease as the C76 content increased. These results were also consistent with Lee’s study in which adding mesoporous carbon to mesoporous WO3 displayed improved charge transfer kinetics towards VO2+/VO2+35. This unraveled the fact that the positive reaction might be much more dependent on the conductivity (C=C bonds) of the electrode18,24,35,36,37. It could also be that C76 lowered the overpotential of the reaction by decreasing the organization energy due to the change in coordination geometry between [VO(H2O)5]2+ and [VO2(H2O)4]+. This, however, might not be achieved with the HWO electrode.

(a) The cyclic voltammetry behavior (at ν = 5 mV/s) of the UCC and HWO-C76 composites with different HWO:C76 ratios for VO2+/VO2+ reactions in 0.1 M VOSO4/1 M H2SO4 + 1 M HCl electrolyte. (b) Randles–Sevcik and (c) Nicholson’s methods for VO2+/VO2+, to estimate the diffusion efficiency and obtain the k0 values (d).

HWO-50% C76 was not only found to exhibit nearly the same electrocatalytic activity of C76 towards the VO2+/VO2+ reaction but more interestingly further inhibited the chlorine evolution, relative to C76, as shown in Fig. 6a, in addition to displaying a smaller semicircle (lower RCT) in Fig. 6d. The C76 showed a higher apparent Ipa/Ipc ratio than HWO-50% C76 (Table S3), not due to the improvement in the reaction reversibility but due to the overlap with the chlorine reduction reaction peak at 1.2 V vs. SHE. The optimum performance of HWO-50% C76 is attributed to the synergistic effect between the negatively charged, highly conductive C76 and the high wettability and W-OH catalyzing functional group on HWO. Whereas less chlorine evolution would enhance the charge efficiency of the full cell, the enhanced kinetics would boost the full cell voltage efficiency.

According to Equation S1, for quasi-reversible (relatively sluggish electron transfer) diffusion-controlled reactions, the peak current (IP) depends on the number of electrons (n), the electrode area (A), the diffusion coefficient (D), the electron transfer coefficient (α), and scan rate (ν). To check the diffusion-controlled behavior of the tested material, the relation between IP versus ν1/2 was plotted and presented in Fig. 6b. Since all materials showed a linear relation the reaction is diffusion-controlled. Since the VO2+/VO2+ reaction is quasi-reversible, the slope of the lines depends on both the diffusion coefficient and the α value (Equation S1). Since the diffusion coefficient is constant (≈ 4 × 10–6 cm2/s)52, the difference in the lines' slop is a direct indication of different α values and hence different electron transfer rates at the electrode surface, with the C76 and HWO-50%C76 showing the steepest slop (the highest electron transfer rate).

The calculated Warburg (W) slopes, at low frequencies, (Fig. 6d) that are reported in Table S3, have values close to one for all the materials, indicating the ideal diffusion of the redox species and confirming the linear behavior of the IP versus ν1/2 of the CV measurements. For the HWO-50% C76, the Warburg slope deviated from unity to1.32, indicating the contribution of not only the semi-infinite diffusion of the reactants (VO2+) but possibly also a thin layer behavior to the diffusion behavior, due to the electrode porosity.

To further analyze the reversibility (electron transfer rate) of the VO2+/VO2+ redox reaction, Nicholson’s method for quasi-reversible reactions was also used to determine the standard rate constant, k041,42. This was done by plotting a dimensionless kinetic parameter, Ψ, which is a function of ΔEp, against ν−1/2 using equations S2. Table S4 shows the values of Ψ obtained for each electrode material. The results were plotted (Fig. 6c) to obtain k0 × 104 cm/s (written next to each line and reported in Table S4) from the slope of each graph using Equation S3. The HWO-50% C76 was found to exhibit the highest slope (Fig. 6c), hence the highest k0 of 2.47 × 10–4 cm/s. This implied that this electrode achieved the fastest kinetics, in line with the CV and EIS results in Fig. 6a and d and Table S3. Besides, k0 values were also obtained from the Nyquist plots (Fig. 6d) using RCT values (Table S3) via Equation S4. These results of k0 from EIS are summarized in Table S4, and also show that HWO-50% C76 exhibited the highest electron transfer rate, owing to the synergistic effects. Even though k0 values were not the same due to the different derivations of each method, they still displayed the same order of magnitude and showed consistency.

To have a complete picture of the achieved superior kinetics, it was important to compare the best electrode material with bare UCC and TCC electrodes. For the VO2+/VO2+ reaction, HWO-C76 did not only display the lowest ΔEp and the best reversibility, but also a significant inhibition of the chlorine evolution parasitic reaction relative to TCC, as seen by the significant drop of current at 1.45 V vs. SHE (Fig. 7a). Regarding the stability, since the catalyst was blended with PVDF binder, and then loaded on the carbon cloth electrode, we assumed that the HWO-50% C76 is physically stable. HWO-50% C76 showed a peak shift equal to 44 mV after 150 cycles (degradation rate 0.29 mV/cycle), in comparison with 50 mV for UCC (Fig. 7b). This might not be a massive difference, but the kinetics of the UCC electrode was very sluggish and tend to get worse with cycling, especially for the backward reaction. Even though the reversibility of TCC was much better than that of UCC, TCC was found to have a large peak shift of 73 mV after 150 cycles, which could be attributed to a large amount of chlorine evolving on its surface. to make sure that the catalyst will adhere well to the electrode surface. As could be seen for all the tested electrodes, even those with no loaded catalyst, showed cyclic instability to a different extent, indicating that the change in peak separation with cycling is due to the deactivation of the material due to chemical changes, not the catalyst detachment. Furthermore, if a significant amount of the catalyst particles was detached from the electrode surface, it would cause a significant increase in the peak separation (not only 44 mV) since the substrate (UCC) is relatively inactive toward VO2+/VO2+ redox reaction.

A comparison between the CV of the best electrode materials relative to UCC (a) and stability (b) for VO2+/VO2+ redox reaction. All CVs were at ν = 5 mV/s in 0.1 M VOSO4/1 M H2SO4 + 1 M HCl electrolyte.

To boost the economic appeal of the VRFB technology, enhancing and understanding the kinetics of vanadium redox reactions is extremely important to achieve high energy efficiency. HWO-C76 composites were fabricated and their electrocatalytic effects were investigated for the VO2+/VO2+ reaction. HWO showed a slight kinetics enhancement but a significant chlorine evolution inhibition in the mixed acid electrolyte. To further optimize the kinetics of HWO-based electrodes, different HWO:C76 ratios were used. Increasing the C76 content to HWO enhanced the electron transfer kinetics of the VO2+/VO2+ reaction on the modified electrode, with HWO-50% C76 being the optimum material as it decreased the charge transfer resistance and further inhibited chlorine evolution relative to C76 and TCC. This was ascribed to the synergistic effects between C=C sp2 hybridization, O–H, and W-OH functional groups. The degradation rate upon repetitive cycling for HWO-50% C76 was found to be 0.29 mV/cycle, compared to 0.33 mV/cycle and 0.49 mV/cycle for UCC and TCC, respectively, rendering it its high stability in the mixed acid electrolyte. The presented results successfully identified high-performance electrode materials for the VO2+/VO2+ reaction with fast kinetics and high stability. This would increase the output voltage and hence the energy efficiency of VRFBs, thereby decreasing their cost for future commercialization.

The datasets used and/or analyzed during the current study are available from the corresponding author on reasonable request.

Luderer, G. et al. Assessment of wind and solar power in global low-carbon energy scenarios: An introduction. Energy Econ. 64, 542–551. https://doi.org/10.1016/j.eneco.2017.03.027 (2017).

Article Google Scholar

Lee, H. J., Park, S. & Kim, H. Analysis of the effect of MnO2 precipitation on the performance of a vanadium/manganese redox flow battery. J. Electrochem. Soc. 165(5), A952–A956. https://doi.org/10.1149/2.0881805jes (2018).

Article CAS Google Scholar

Shah, A. A., Tangirala, R., Singh, R., Wills, R. G. A. & Walsh, F. C. A dynamic unit cell model for the all-vanadium flow battery. J. Electrochem. Soc. 158(6), A671. https://doi.org/10.1149/1.3561426 (2011).

Article CAS Google Scholar

Mongird, K. et al. 2020 Grid Energy Storage Technology Cost and Performance Assessment (2020).

Gandomi, Y. A., Aaron, D. S., Zawodzinski, T. A. & Mench, M. M. In situ potential distribution measurement and validated model for all-vanadium redox flow battery. J. Electrochem. Soc. 163(1), A5188–A5201. https://doi.org/10.1149/2.0211601jes (2016).

Article CAS Google Scholar

Tsushima, S. & Suzuki, T. Modeling and simulation of vanadium redox flow battery with interdigitated flow field for optimizing electrode architecture. J. Electrochem. Soc. 167(2), 020553. https://doi.org/10.1149/1945-7111/ab6dd0 (2020).

Article ADS CAS Google Scholar

Sun, B. & Skyllas-Kazacos, M. Modification of graphite electrode materials for vanadium redox flow battery application—I. Thermal treatment. Electrochim. Acta 37(7), 1253–1260. https://doi.org/10.1016/0013-4686(92)85064-R (1992).

Article CAS Google Scholar

Liu, T., Li, X., Zhang, H. & Chen, J. Progress on the electrode materials towards vanadium flow batteries (VFBs) with improved power density. J. Energy Chem. 27(5), 1292–1303. https://doi.org/10.1016/j.jechem.2018.07.003 (2018).

Article Google Scholar

Liu, Q. H. et al. High performance vanadium redox flow batteries with optimized electrode configuration and membrane selection. J. Electrochem. Soc. 159(8), A1246–A1252. https://doi.org/10.1149/2.051208jes (2012).

Article CAS Google Scholar

Wei, G., Jia, C., Liu, J. & Yan, C. Carbon felt supported carbon nanotubes catalysts composite electrode for vanadium redox flow battery application. J. Power Sourc. 220, 185–192. https://doi.org/10.1016/j.jpowsour.2012.07.081 (2012).

Article ADS CAS Google Scholar

Moon, S., Kwon, B. W., Chung, Y. & Kwon, Y. Effect of bismuth sulfate coated on acidified CNT on performance of vanadium redox flow battery. J. Electrochem. Soc. 166(12), A2602. https://doi.org/10.1149/2.1181912jes (2019).

Article CAS Google Scholar

Huang, R.-H. et al. Investigation of active electrodes modified with platinum/multiwalled carbon nanotube for vanadium redox flow battery. J. Electrochem. Soc. 159(10), A1579. https://doi.org/10.1149/2.003210jes (2012).

Article CAS Google Scholar

Noh, C. et al. Vanadium redox flow battery using electrocatalyst decorated with nitrogen-doped carbon nanotubes derived from metal-organic frameworks. J. Electrochem. Soc. 165(7), A1388. https://doi.org/10.1149/2.0621807jes (2018).

Article CAS Google Scholar

Han, P. et al. Graphene oxide nanoplatelets as excellent electrochemical active materials for VO2+/ and V2+/V3+ redox couples for a vanadium redox flow battery. Carbon 49(2), 693–700. https://doi.org/10.1016/j.carbon.2010.10.022 (2011).

Article CAS Google Scholar

González, Z. et al. Outstanding electrochemical performance of a graphene-modified graphite felt for vanadium redox flow battery application. J. Power Sourc. 338, 155–162. https://doi.org/10.1016/j.jpowsour.2016.10.069 (2017).

Article ADS CAS Google Scholar

González, Z., Vizireanu, S., Dinescu, G., Blanco, C. & Santamaría, R. Carbon nanowalls thin films as nanostructured electrode materials in vanadium redox flow batteries. Nano Energy 1(6), 833–839. https://doi.org/10.1016/j.nanoen.2012.07.003 (2012).

Article CAS Google Scholar

Opar, D. O., Nankya, R., Lee, J. & Jung, H. Three-dimensional mesoporous graphene-modified carbon felt for high-performance vanadium redox flow batteries. Electrochim. Acta 330, 135276. https://doi.org/10.1016/j.electacta.2019.135276 (2020).

Article CAS Google Scholar

He, Z. et al. Carbon nanofibers grown on the surface of graphite felt by chemical vapour deposition for vanadium redox flow batteries. RSC Adv. 3(43), 19774. https://doi.org/10.1039/c3ra22631j (2013).

Article ADS CAS Google Scholar

Sodiq, A. et al. Black pearl carbon as a catalyst for all-vanadium redox flow batteries. Chem. Commun. 55(69), 10249–10252. https://doi.org/10.1039/C9CC03640G (2019).

Article CAS Google Scholar

Jeong, S., An, S., Jeong, J., Lee, J. & Kwon, Y. Effect of mesocelluar carbon foam electrode material on performance of vanadium redox flow battery. J. Power Sourc. 278, 245–254. https://doi.org/10.1016/j.jpowsour.2014.12.074 (2015).

Article ADS CAS Google Scholar

Gao, Y. et al. Carbon sheet-decorated graphite felt electrode with high catalytic activity for vanadium redox flow batteries. Carbon 148, 9–15. https://doi.org/10.1016/j.carbon.2019.03.035 (2019).

Article CAS Google Scholar

Park, M., Ryu, J., Kim, Y. & Cho, J. Corn protein-derived nitrogen-doped carbon materials with oxygen-rich functional groups: A highly efficient electrocatalyst for all-vanadium redox flow batteries. Energy Env. Sci. 7(11), 3727–3735. https://doi.org/10.1039/C4EE02123A (2014).

Article CAS Google Scholar

Wang, R. & Li, Y. Twin-cocoon-derived self-standing nitrogen-oxygen-rich monolithic carbon material as the cost-effective electrode for redox flow batteries. J. Power Sourc. 421, 139–146. https://doi.org/10.1016/j.jpowsour.2019.03.023 (2019).

Article ADS CAS Google Scholar

Diwany, F. A. E., Ali, B. A., Sawy, E. N. E. & Allam, N. K. Fullerene C76 as a novel electrocatalyst for VO2+/VO2+ and chlorine evolution inhibitor in all-vanadium redox flow batteries. Chem. Commun. 56(55), 7569–7572. https://doi.org/10.1039/D0CC03544K (2020).

Article Google Scholar

Zhou, H. et al. CeO2 decorated graphite felt as a high-performance electrode for vanadium redox flow batteries. RSC Adv. 4(106), 61912–61918. https://doi.org/10.1039/C4RA12339E (2014).

Article ADS CAS Google Scholar

Zhou, H., Shen, Y., Xi, J., Qiu, X. & Chen, L. ZrO2-nanoparticle-modified graphite felt: Bifunctional effects on vanadium flow batteries. ACS Appl. Mater. Interfaces 8(24), 15369–15378. https://doi.org/10.1021/acsami.6b03761 (2016).

Article CAS PubMed Google Scholar

Cao, L., Skyllas-Kazacos, M. & Wang, D.-W. Modification based on MoO3 as electrocatalysts for high power density vanadium redox flow batteries. ChemElectroChem 4(8), 1836–1839. https://doi.org/10.1002/celc.201700376 (2017).

Article CAS Google Scholar

Yun, N., Park, J. J., Park, O. O., Lee, K. B. & Yang, J. H. Electrocatalytic effect of NiO nanoparticles evenly distributed on a graphite felt electrode for vanadium redox flow batteries. Electrochim. Acta 278, 226–235. https://doi.org/10.1016/j.electacta.2018.05.039 (2018).

Article CAS Google Scholar

Mehboob, S. et al. Enhancing the performance of all-vanadium redox flow batteries by decorating carbon felt electrodes with SnO2 nanoparticles. Appl. Energy 229, 910–921. https://doi.org/10.1016/j.apenergy.2018.08.047 (2018).

Article CAS Google Scholar

Xiang, Y. & Daoud, W. A. Cr2O3-modified graphite felt as a novel positive electrode for vanadium redox flow battery. Electrochim. Acta 290, 176–184. https://doi.org/10.1016/j.electacta.2018.09.023 (2018).

Article CAS Google Scholar

Yao, C., Zhang, H., Liu, T., Li, X. & Liu, Z. Carbon paper coated with supported tungsten trioxide as novel electrode for all-vanadium flow battery. J. Power Sourc. 218, 455–461. https://doi.org/10.1016/j.jpowsour.2012.06.072 (2012).

Article ADS CAS Google Scholar

Shen, Y. et al. Electrochemical catalytic activity of tungsten trioxide-modified graphite felt toward VO2+/VO2+ redox reaction. Electrochim. Acta 132, 37–41. https://doi.org/10.1016/j.electacta.2014.03.107 (2014).

Article ADS CAS Google Scholar

Kabtamu, D. M., Chen, J.-Y., Chang, Y.-C. & Wang, C.-H. Electrocatalytic activity of Nb-doped hexagonal WO3 nanowire-modified graphite felt as a positive electrode for vanadium redox flow batteries. J. Mater. Chem. A 4(29), 11472–11480. https://doi.org/10.1039/C6TA03936G (2016).

Article CAS Google Scholar

Hosseini, M. G. et al. High-power positive electrode based on synergistic effect of N- and WO3-decorated carbon felt for vanadium redox flow batteries. Carbon 136, 444–453. https://doi.org/10.1016/j.carbon.2018.04.038 (2018).

Article CAS Google Scholar

Lee, W. et al. Mesoporous tungsten oxynitride as electrocatalyst for promoting redox reactions of vanadium redox couple and performance of vanadium redox flow battery. Appl. Surf. Sci. 429, 187–195. https://doi.org/10.1016/j.apsusc.2017.07.022 (2018).

Article ADS CAS Google Scholar

Faraji, M., Khalilzadeh Soltanahmadi, R., Seyfi, S., Mostafavi Bavani, B. & Mohammadzadeh Aydisheh, H. Highly porous WO3/CNTs-graphite film as a novel and low-cost positive electrode for vanadium redox flow battery. J. Solid State Electrochem. 24(10), 2315–2324. https://doi.org/10.1007/s10008-020-04671-6 (2020).

Article CAS Google Scholar

Kabtamu, D. M. et al. Three-dimensional annealed WO3 nanowire/graphene foam as an electrocatalytic material for all vanadium redox flow batteries. Sustain. Energy Fuels 1(10), 2091–2100. https://doi.org/10.1039/C7SE00271H (2017).

Article CAS Google Scholar

Bayeh, A. W. et al. Hydrogen-treated defect-rich W18O49 nanowire-modified graphite felt as high-performance electrode for vanadium redox flow battery. ACS Appl. Energy Mater. 2(4), 2541–2551. https://doi.org/10.1021/acsaem.8b02158 (2019).

Article CAS Google Scholar

Farsi, H., Gobal, F. & Barzgari, Z. A study of hydrated nanostructured tungsten trioxide as an electroactive material for pseudocapacitors. Ionics 19(2), 287–294. https://doi.org/10.1007/s11581-012-0726-8 (2013).

Article CAS Google Scholar

Mitchell, J. B., Lo, W. C., Genc, A., LeBeau, J. & Augustyn, V. Transition from battery to pseudocapacitor behavior via structural water in tungsten oxide. Chem. Mater. 29(9), 3928–3937. https://doi.org/10.1021/acs.chemmater.6b05485 (2017).

Article CAS Google Scholar

Iwakiri, I. et al. Redox flow batteries: Materials, design and prospects. Energies 14(18), 5643. https://doi.org/10.3390/en14185643 (2021).

Article CAS Google Scholar

Li, L. et al. A stable vanadium redox-flow battery with high energy density for large-scale energy storage. Adv. Energy Mater. 1(3), 394–400. https://doi.org/10.1002/aenm.201100008 (2011).

Article CAS Google Scholar

Songara, S. et al. Tuning of crystal phase structure in hydrated WO3 nanoparticles under wet chemical conditions and studies on their photochromic properties. J. Phys. Chem. Solids 73(7), 851–857. https://doi.org/10.1016/j.jpcs.2012.02.020 (2012).

Article ADS CAS Google Scholar

Klinger, M. & Jäger, A. Crystallographic tool box (CrysTBox): Automated tools for transmission electron microscopists and crystallographers. J. Appl. Crystallogr. 48(6), 2012–2018. https://doi.org/10.1107/S1600576715017252 (2015).

Article CAS PubMed PubMed Central Google Scholar

Degen, T., Sadki, M., Bron, E., König, U. & Nénert, G. The high score suite. Powder Diffr. 29(S2), S13–S18. https://doi.org/10.1017/S0885715614000840 (2014).

Article ADS CAS Google Scholar

Nicholson, R. S. Theory and application of cyclic voltammetry for measurement of electrode reaction kinetics. Anal. Chem. 37(11), 1351–1355. https://doi.org/10.1021/ac60230a016 (1965).

Article CAS Google Scholar

Lavagnini, I., Antiochia, R. & Magno, F. An extended method for the practical evaluation of the standard rate constant from cyclic voltammetric data. Electroanalysis 16(6), 505–506. https://doi.org/10.1002/elan.200302851 (2004).

Article CAS Google Scholar

Ling, M. & Blackman, C. S. Gas-phase synthesis of hybrid nanostructured materials. Nanoscale 10(48), 22981–22989. https://doi.org/10.1039/C8NR06257A (2018).

Article CAS PubMed Google Scholar

Ling, M. Tungsten Oxide and Tungsten Oxide Based Heterogeneous Nanostructure Thin Films: Synthesis via AACVD, Characterisation, Growth Mechanism, and Application in Photocatalysis 183 (2020).

Kawada, H. et al. Structural aspects of C82 and C76 crystals studied by X-Ray diffraction. Phys. Rev. B 51(14), 8723–8730. https://doi.org/10.1103/PhysRevB.51.8723 (1995).

Article ADS CAS Google Scholar

Hassaneen, F. Y. et al. Innovative nanocomposite formulations for enhancing biogas and biofertilizers production from anaerobic digestion of organic waste. Bioresour. Technol. 309, 123350. https://doi.org/10.1016/j.biortech.2020.123350 (2020).

Article CAS PubMed Google Scholar

Jiang, Z., Klyukin, K. & Alexandrov, V. Structure, hydrolysis, and diffusion of aqueous vanadium ions from car-parrinello molecular dynamics. J. Chem. Phys. 145(11), 114303. https://doi.org/10.1063/1.4962748 (2016).

Article ADS CAS Google Scholar

Download references

The authors would like to thank Mohamed Salama for the SEM imaging, and Nashaat Ahmed and Dr. Ayat El Shazly for the XRD, FTIR, and XPS measurements. The authors are thankful to the American University in Cairo for supporting this work.

Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB). This work were supported by American University in Cairo, SSE-CHEM-E.E.-FY19-FY20-FY21-RG(1-19)-2018-Oct-01-20-37-05.

Department of Chemistry, School of Sciences and Engineering, The American University in Cairo, New Cairo, 11835, Egypt

Farah A. El Diwany, Taher Al Najjar & Ehab N. El Sawy

Energy Materials Laboratory, School of Sciences and Engineering, The American University in Cairo, New Cairo, 11835, Egypt

Farah A. El Diwany & Nageh K. Allam

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

F.A.E. did most of the experimental work, analyzed the results, and wrote the first draft of the paper. T.A. helped in the experimental work and revised the first draft. E.E. and N.A. provided the conceptual plan, supervised the work, secured the funding, and revised the manuscript.

Correspondence to Nageh K. Allam or Ehab N. El Sawy.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

El Diwany, F.A., Al Najjar, T., Allam, N.K. et al. Tungsten oxide/fullerene-based nanocomposites as electrocatalysts and parasitic reactions inhibitors for VO2+/VO2+ in mixed-acids. Sci Rep 12, 14348 (2022). https://doi.org/10.1038/s41598-022-18561-6

Download citation

Received: 13 June 2022

Accepted: 16 August 2022

Published: 23 August 2022

DOI: https://doi.org/10.1038/s41598-022-18561-6

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Journal of Materials Science: Materials in Electronics (2023)

Journal of Materials Science (2022)