Scientific Reports volume 13, Article number: 12810 (2023) Cite this article

Metrics details

Intrigued by the discovery of the long lifetime in the α-Ta/Al2O3-based Transmon qubit, researchers recently found α-Ta film is a promising platform for fabricating multi-qubits with long coherence time. To meet the requirements for integrating superconducting quantum circuits, the ideal method is to grow α-Ta film on a silicon substrate compatible with industrial manufacturing. Here we report the α-Ta film sputter-grown on Si (100) with a low-loss superconducting TiNx buffer layer. The α-Ta film with a large growth temperature window has a good crystalline character. The superconducting critical transition temperature (Tc) and residual resistivity ratio (RRR) in the α-Ta film grown at 500 °C are higher than that in the α-Ta film grown at room temperature (RT). These results provide crucial experimental clues toward understanding the connection between the superconductivity and the materials' properties in the α-Ta film and open a new route for producing a high-quality α-Ta film on silicon substrate for future industrial superconducting quantum computers.

Superconducting materials grown on Si or Al2O3 substrates may form films of high crystallinity and with inherently low dielectric loss, thus are explored as the materials for building superconducting quantum circuits1,2,3,4,5,6. Recently, researchers have made efforts to search for new superconducting films with stable superconducting properties and mature processing used in the quantum computing field, aiming to improve the performance of superconducting qubits, including long coherence time and fast gates5,7,8,9,10,11,12. The high-quality superconducting films with low dielectric losses at surfaces and interfaces which exhibit high RRR are promising for the fabrication of high-performance qubits1,2,7,13,14. Specially, using α-Ta films to fabricate the 2D Transmons, the devices have shown a significant improvement in performance arising from the lower surface-related loss7,8. Thus, the α-Ta film is a promising base superconductor to build large-scale superconducting quantum circuits with high-performance properties, paving the way toward practical superconducting quantum computers. However, in these superconducting qubits studies7,8, the sapphire substrate which was used to grow α-Ta film cannot be easily scaled-up with advanced integration, such as the through via technology. By contrast, the silicon substrate is widely used for large-scale integrated circuits. It is therefore very natural to raise the question of whether α-Ta film can be grown on a silicon substrate or not.

The obtainment of α-Ta film which is easily formed at high temperature deposited on Si substrate without inner-diffusion interface is very limited, partially because of the obstacle that Ta is highly reactive to the heating Si substrate15,16,17. Although it has been reported that the α-Ta film is deposited on Si substrate at RT successfully by using several strategies such as optimizing the sputtering conditions and adding under layers18,19,20,21,22,23,24,25,26,27,28,29,30. In comparison to high-temperature growth, these films are more likely to have smaller grain sizes, more grain boundaries, and more surface defects as a result of RT deposition18,19,20,21,22, which might lead to an additional dielectric loss in the superconducting quantum device8,12,13,14,31,32,33. Besides, in these studies, the Ta-Si interface may include thicker non-superconducting underlayers25,27 or metal silicides15,16,17 which might form because of heating treatments used during the device fabrication flow. This would increase microwave loss channels at interfaces12,13,31,32,33. Thus, we need a new method to grow α-Ta film on the Si substrate that has a large grain size and clear interface with low-loss superconducting buffer layers while minimizing dielectric loss at surfaces and interfaces to improve superconducting qubit performance.

Here, we systematically investigated the quality and superconductivity of α-Ta film prepared on a superconducting TiNx buffer layer deposited on Si (100) substrate. Previous studies have demonstrated that a significant improvement in the performance of superconducting quantum circuits can be achieved by using TiNx as the base superconductor in the capacitor and microwave resonators, illustrating TiNx film have a low dielectric loss34,35. α-Ta films were formed at different temperatures varied from RT to 500 °C, directly suggesting a large processing temperature window. This is in sharp contrast to previous studies19,20,21,22,23, in which the preparation of α-Ta film was under RT conditions. The crystal quality of the α-Ta film was improved by increasing the growth temperature. Meanwhile, the difference in the growing temperature has no effect either on the low intensity of contaminants in the α-Ta films or on the clean and sharp interface between Si and Ta due to the presence of the TiNx buffer layer. Furthermore, we observed the zero resistance and measured RRR in the α-Ta film. Notably, RRR found in α-Ta films grown at 500 °C is remarkably higher than that in α-Ta grown at RT, which possibly be attributed to the large grain size and the suppression of surface defects.

α-Ta possesses a cubic structure with the lattice parameter a = 0.33 nm19,20. To synthesize high-quality α-Ta films on high resistivity 2 inches Si(100) substrates (its resistivity value > 10 kΩ cm), a two-step method was applied. First, the low-loss superconducting TiNx buffer layer, 3~5 nm thick was deposited by dc reactive magnetron sputtering using 2 inches Ti (purity of 99.995%) target and N2 (purity of 99.999%) reactive gas. After cleaning the substrates with wet chemicals (see “Wet chemical processes of Si substrates” in the Supplementary Information), they were thermally cleaned inside the growth chamber at 500 °C for 30 min. Then, the substrates were cooled down to room temperature at 30 °C per minute. During the TiNx deposition, the substrate temperature was held at RT, while a constant pressure of 2 mTorr was maintained in the presence of Ar and N2, flowing at 10 sccm and 15 sccm respectively. The power of the DC generator was 100 W. After TiNx of deposition, the α-Ta films were prepared on the TiNx buffer layers under different temperatures while the Ar pressure was kept at 5.25 mTorr with a gas flow of 20 sccm, and the power of the DC generator was 200 W.

The crystal structure and phases of the α-Ta film were analyzed using X-Ray Diffraction (XRD). Figure 1 shows the XRD of α-Ta films grown on TiNx buffer layers (The information about the TiNx buffer layer is in the Supplementary Information) at different temperatures. It can be cleanly seen that the dominative features of α-Ta films are the (110) and (220) diffraction peaks near 38.1° and 81.5° respectively. In addition, the weak α-Ta (100) peaks at 54.8° are visible [Fig. 1b]. Apart from strong dominant diffraction peaks of α-Ta, only a very tiny diffraction peak of β-Ta is observed at 34.6°, suggesting within a wide temperature range, a major α-phase Ta film on Si (100) substrate was deposited successfully. This is most likely because of TiNx buffer layer promoted the growth of α-Ta film due to its reducing lattice mismatch19,20. Furthermore, as the temperature increased, not only the relative intensity of the main (110) peak became stronger, also its full width at half maximum (FWHM) became sharper. This measurement result is direct evidence for the grain size increase with increasing temperature, which is consistent with the previous report20, indicating a high temperature led to the good crystallization of α-Ta film.

(a) XRD pattern of α-Ta films deposited on TiNx/Si at different temperatures ranging from RT to 500 °C. The curves are shifted upward for a better display. (b) and (c) Enlarged XRD pattern near (110) peaks and (220) peaks shown in (a). The intensities are plotted on a logarithmic scale to see the important behavior at lower intensities shown in (b) and (c).

The quality of the sample surface was investigated with Atomic Force Microscope (AFM). The surface morphologies of α-Ta films grown on TiNx buffer layers at RT- 500 °C temperature range are revealed in typical large-scale AFM images (Fig. 2). At RT, the small round grains can be seen on the surface. With the substrate temperature increasing, elongated-like grains start to be obvious, as shown in Fig. 2b. However, the surface [Fig. 2c] of the α-Ta film deposited at 300 °C is visually different. A typical needle-shape feature of the grains is evident. At 400 °C, a tight network of elongated needle-shaped grains uniformly distributed across the surface [Fig. 2d]. Compared to the one sputter deposited at 300 °C, the size of the needle-shaped grains at 400 °C is wider and more homogeneous. Next at 500 °C, as shown in Fig. 2e, the grains look elongated, highly homogeneous in size and uniformly distributed on the surface. Moreover, the density of defects such as holes with varying size and depth in the surface of α-Ta grown at RT are much higher than these of α-Ta films grown at high temperatures. Figure 2f–g reveal that α-Ta films deposited at RT and 500 °C are highly dense and not porous, which suggests holes observed from AFM images only appear on the surface. These results reflect substrate temperature plays a critical role in controlling the surface morphology of the α-Ta film. The difference in the topographic feature is answerable for the different quality of macroscopic electrical transport properties in the films as discussed below.

AFM images and cross section TEM of α-Ta/Si at different temperatures. (a, f) RT, (b) 150 °C, (c) 300 °C, (d) 400 °C, (e, f) 500 °C. White arrows are used for guiding holes in (a) and (e).

Close microstructure analysis near the hetero-interface between α-Ta film and Si by high-resolution high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and Energy Dispersive Spectrometer (EDS) is shown in Fig. 3. For α-Ta film grown at RT, the HAADF-STEM micrograph revealed that there is about 5 nm TiNx buffer layer between the Ta film and the Si substrate [Fig. 3a]. Additionally, the TiNx buffer layer growth on the bare Si substrates is correlated with the formation of an amorphous layer (1~2 nm thick) during the pre-deposition procedure, which is consistent with previous reports36 (Supplementary Information Fig. S3). It has been reported that TiNx film can provide low dielectric loss in superconducting quantum computing systems34,35. And so it is reasonable to consider that if using α-Ta film deposited on the TiNx buffer layer as a material platform to build superconducting qubits, the TiNx buffer layer would not lead to additional dielectric loss. The EDS elemental maps of Si and Ta, as shown in Fig. 3b,c, exhibit step functions of the chemistry changes across the interfaces, illustrating that no intermixing of Ta and Si occurred between the α-Ta film and Si substrate. With respect to α-Ta film grown at 500 °C, similarly, Si and Ta’ signals sharply change across the Ta/Si interface as shown in Fig. 3e and f. It should be concluded that no inter-diffusion in the Ta/Si interface at 500 °C, which is different from previous studies15,16,17. This result suggests the TiNx buffer layer is thermodynamically stable and dense, and therefore could prevent intermixing of Ta and Si between α-Ta film and Si substrate under high substrate temperature. It is noted that the backgrounds of EDS maps in these two samples are different, which might correlate to the different concentrations of contaminants introduced during the SEM sample preparation process.

Ta-Si interface of α-Ta/Si films grown at RT (a–c) and 500 °C (d–f). (a, d) High resolution HAADF-STEM images showing Ta-Si interface; (b–c, e–f) EDS maps of Ta and Si.

The time of flight secondary ion mass spectroscopy (TOF-SIMS) results of the Ta films deposited at RT and 500 °C are shown in Fig. 4. Here, in order to directly compare the relative concentrations between the samples, all the signals are normalized by the intensity of Ta in the Ta layer region. These two samples both have almost the same Si, Ta, TiNx, and TaOx profiles with sharp changes in the Ta/Si interfaces, showing no intermixing of Ta, TiNx, Ti, and Si components. The result is directly evidenced that even heating to 500 °C, the Ta/TiNx and TiNx/Si interfaces in the α-Ta film are as sharp and clean as that in the α-Ta film grown at RT, indicating the versatility of 5 nm thick TiNx buffer layer as discussed above. Meanwhile, the distribution of contaminants such as H, C and O in the bulk of films of these two samples are detected. As shown in Fig. 4c and d, similar O, C and H profiles are also observed. In addition, their concentrations are just above the detection levels. Based on this discussion, we can conclude that the insignificant intensity of contaminants is nearly the same in the bulk of these two films.

TOF-SIMS depth profiles of α-Ta/Si films deposited at (a, b) RT and (c, d) 500 °C respectively. The intensities are plotted on a logarithmic scale to see the important behavior at lower intensities.

The electrical properties were detected from the two α-Ta films grown at RT and 500 °C with four-point probe measurements. The resistivity measured as a function of temperature is shown in Fig. 5. The Tc values are found to be 3.8 and 3.9 K for samples grown at RT and at 500 °C respectively. These Tc values are comparable to that of the bulk α-Ta but much higher than that of the bulk β-Ta (Tc < 1), directly verifying the deposited Ta film is in the α phase, which is consistent with the above XRD results. For the α-Ta film grown at 500 °C, its RRR value (RRR = ρ(300 K)/ρ(5 K)) is 3.85. Compared to α-Ta film grown at RT, where RRR = 1.85, the RRR value of α-Ta film grown at 500 °C is much higher and the resistivity much smaller. This is likely due to the larger grain sizes and the existence of fewer defects37,38,39,40 rather than the presence of contaminants in the α-Ta film grown at 500 °C, which have been discussed above. Moreover, according to earlier studies13,39,40, a higher RRR in the α-Ta film grown at 500 °C render it more suitable as a base material for superconducting multi-qubits.

Temperature dependence of the electrical transport properties for α-Ta films deposited at (a) RT and (b) 500 °C respectively. The inset shows R-T curve near Tc.

In summary, the α-Ta film deposited on Si(100) substrate with low-loss superconducting TiNx buffer layer has been studied comprehensively. The XRD results and AFM surface images show that good crystallization of α-Ta film with fewer surface defects was achieved by substrate temperature optimization. The identical low impurity concentrations and similar sharp Ta/Si interfaces with no inter-diffusion at various substrate temperatures indicate that the low-loss superconducting TiNx buffer layer is the dominant factor in the growth of the α-Ta film. The Tc and RRR values in the α-Ta films are revealed by analyzing R-T curves. The increase in Tc and RRR values is associated with the increase in grain size and the decrease in surface defects, providing a new hint to the correlation between the nature of superconductivity and the quality of the α-Ta film. Our result here shows that by manipulating the film growth, α-Ta film on Si(100) substrate with a sharp interface can be synthesized in both high quality and strong superconducting state, thus making it suitable to be used in large-scale superconducting qubit devices.

The data that support the findings of this study are available from the corresponding author upon reasonable request.

de Leon, N. P. et al. Materials challenges and opportunities for quantum computing hardware. Science 372, eabb2823. https://doi.org/10.1126/science.abb2823 (2021).

Article ADS CAS PubMed Google Scholar

Murray, C. E. Material matters in superconducting qubits. Mater. Sci. Eng. R Rep. 146, 100646. https://doi.org/10.1016/j.mser.2021.100646 (2021).

Article Google Scholar

McRae, C. R. H. et al. Materials loss measurements using superconducting microwave resonators. Rev. Sci. Instrum. 91, 091101. https://doi.org/10.1063/5.0017378 (2020).

Article ADS CAS PubMed Google Scholar

Megrant, J. M. M. a. A. UCSB final report for the CSQ program: Review of decoherence and materials physics for superconducting qubits. arXiv preprint arXiv:1410.5793, https://doi/org/https://doi.org/10.48550/arXiv.1410.5793 (2014).

Xiong, K. et al. Materials in superconducting quantum circuits. Chin. Sci. Bull. 67, 143. https://doi.org/10.1360/tb-2021-0479 (2021).

Article Google Scholar

Qiu, W. & Terai, H. Fabrication of deep-sub-micrometer NbN/AlN/NbN epitaxial junctions on a Si-substrate. Appl. Phys. Express 13, 126501. https://doi.org/10.35848/1882-0786/abbfde (2020).

Article ADS CAS Google Scholar

Place, A. P. M. et al. New material platform for superconducting transmon qubits with coherence times exceeding 0.3 milliseconds. Nat. Commun. 12, 1779. https://doi.org/10.1038/s41467-021-22030-5 (2021).

Article ADS CAS PubMed PubMed Central Google Scholar

Wang, C. et al. Towards practical quantum computers: Transmon qubit with a lifetime approaching 05 milliseconds. NPJ Quant. Inf. 8, 3. https://doi.org/10.1038/s41534-021-00510-2 (2022).

Article ADS Google Scholar

Kim, S. et al. Enhanced coherence of all-nitride superconducting qubits epitaxially grown on silicon substrate. Commun. Mater. 2, 98. https://doi.org/10.1038/s43246-021-00204-4 (2021).

Article CAS Google Scholar

Earnest, C. T. et al. Substrate surface engineering for high-quality silicon/aluminum superconducting resonators. Superconductor Sci. Technol. 31, 125013. https://doi.org/10.1088/1361-6668/aae548 (2018).

Article ADS CAS Google Scholar

Megrant, A. et al. Planar superconducting resonators with internal quality factors above one million. Appl. Phys. Lett. 100, 113510. https://doi.org/10.1063/1.3693409 (2012).

Article ADS CAS Google Scholar

Wang, C. et al. Surface participation and dielectric loss in superconducting qubits. Appl. Phys. Lett. 107, 162601. https://doi.org/10.1063/1.4934486 (2015).

Article ADS CAS Google Scholar

Premkumar, A. et al. Microscopic relaxation channels in materials for superconducting qubits. Commun. Mater. 2, 72. https://doi.org/10.1038/s43246-021-00174-7 (2021).

Article Google Scholar

Siddiqi, I. Engineering high-coherence superconducting qubits. Nat. Rev. Mater. 6, 875–891. https://doi.org/10.1038/s41578-021-00370-4 (2021).

Article ADS Google Scholar

Liu, L. et al. Annealing effects of tantalum thin films sputtered on [001] silicon substrate. Mater. Sci. Eng. C 16, 85–89. https://doi.org/10.1016/S0928-4931(01)00280-6 (2001).

Article Google Scholar

Pelleg, J., Rosenberg, S. & Sinder, M. Heat explosion approach to radiofrequency heating of a conductor film on silicon substrate: Application for silicide film formation. Acta Mater. 59, 4283–4290. https://doi.org/10.1016/j.actamat.2011.03.052 (2011).

Article ADS CAS Google Scholar

Pelleg, J. Formation of Co and Ta silicides on Si(111) and Si(100) substrates from codeposited Co and Ta thin films. Thin Solid Films 325, 60–71. https://doi.org/10.1016/S0040-6090(98)00451-9 (1998).

Article ADS CAS Google Scholar

Latif, R. et al. Influence of tantalum’s crystal phase growth on the microstructural, electrical and mechanical properties of sputter-deposited tantalum thin film layer. Int. J. Refract. Metals Hard Mater. 92, 105314. https://doi.org/10.1016/j.ijrmhm.2020.105314 (2020).

Article CAS Google Scholar

Bernoulli, D., Müller, U., Schwarzenberger, M., Hauert, R. & Spolenak, R. Magnetron sputter deposited tantalum and tantalum nitride thin films: An analysis of phase, hardness and composition. Thin Solid Films 548, 157–161. https://doi.org/10.1016/j.tsf.2013.09.055 (2013).

Article ADS CAS Google Scholar

Navid, A. A. & Hodge, A. M. Nanostructured alpha and beta tantalum formation—Relationship between plasma parameters and microstructure. Mater. Sci. Eng. A 536, 49–56. https://doi.org/10.1016/j.msea.2011.12.017 (2012).

Article CAS Google Scholar

Navid, A. A. & Hodge, A. M. Controllable residual stresses in sputtered nanostructured alpha-tantalum. Scripta Mater. 63, 867–870. https://doi.org/10.1016/j.scriptamat.2010.06.037 (2010).

Article CAS Google Scholar

Ren, H. & Sosnowski, M. Tantalum thin films deposited by ion assisted magnetron sputtering. Thin Solid Films 516, 1898–1905. https://doi.org/10.1016/j.tsf.2007.10.127 (2008).

Article ADS CAS Google Scholar

Chen, G. S., Chen, S. T., Huang, S. C. & Lee, H. Y. Growth mechanism of sputter deposited Ta and Ta–N thin films induced by an underlying titanium layer and varying nitrogen flow rates. Appl. Surf. Sci. 169–170, 353–357. https://doi.org/10.1016/S0169-4332(00)00679-6 (2001).

Article ADS Google Scholar

Clevenger, L. A., Mutscheller, A., Harper, J. M. E., Cabral, C. Jr. & Barmak, K. The relationship between deposition conditions, the beta to alpha phase transformation, and stress relaxation in tantalum thin films. J. Appl. Phys. 72, 4918–4924. https://doi.org/10.1063/1.352059 (1992).

Article ADS CAS Google Scholar

Hoogeveen, R., Moske, M., Geisler, H. & Samwer, K. Texture and phase transformation of sputter-deposited metastable Ta films and TaCu multilayers. Thin Solid Films 275, 203–206. https://doi.org/10.1016/0040-6090(95)07043-5 (1996).

Article ADS CAS Google Scholar

Morohashi, S., Gotoh, K. & Komiya, S. Fabrication of Josephson junctions using an Al/Ta/Nb structure for x-ray detection. Appl. Phys. Lett. 64, 785–787. https://doi.org/10.1063/1.111013 (1994).

Article ADS CAS Google Scholar

Morohashi, S. Ta/w/A10x-AL/ta/Nb josephson junctions for X-ray detector. Jpn. J. Appl. Phys. 34, L1352–L1354. https://doi.org/10.1143/JJAP.34.L1352 (1995).

Article ADS CAS Google Scholar

Face, D. W. & Prober, D. E. Nucleation of body-centered-cubic tantalum films with a thin niobium underlayer. J. Vac. Sci. Technol. A Vac. Surf. Films 5, 3408–3411. https://doi.org/10.1116/1.574203 (1987).

Article ADS CAS Google Scholar

Gamou, H., Ryu, J., Kohda, M. & Nitta, J. Different spin relaxation mechanisms between epitaxial and polycrystalline Ta thin films. Appl. Phys. Express 10, 023003. https://doi.org/10.7567/APEX.10.023003 (2017).

Article ADS Google Scholar

Gladczuk, L., Patel, A., Singh, P. C. & Sosnowski, M. Tantalum films for protective coatings of steel. Thin Solid Films 467, 150–157. https://doi.org/10.1016/j.tsf.2004.04.041 (2004).

Article ADS CAS Google Scholar

Gambetta, J. M. et al. Investigating surface loss effects in superconducting transmon qubits. IEEE Trans. Appl. Supercond. 27, 1–5. https://doi.org/10.1109/TASC.2016.2629670 (2017).

Article Google Scholar

Paik, H. et al. Observation of high coherence in Josephson Junction Qubits measured in a three-dimensional circuit QED architecture. Phys. Rev. Lett. 107, 240501. https://doi.org/10.1103/PhysRevLett.107.240501 (2011).

Article ADS CAS PubMed Google Scholar

Oliver, W. D. & Welander, P. B. Materials in superconducting quantum bits. MRS Bull. 38, 816–825. https://doi.org/10.1557/mrs.2013.229 (2013).

Article CAS Google Scholar

Ohya, S. et al. Room temperature deposition of sputtered TiN films for superconducting coplanar waveguide resonators. Supercond. Sci. Technol. 27, 015009. https://doi.org/10.1088/0953-2048/27/1/015009 (2014).

Article ADS CAS Google Scholar

Deng, H. et al. Titanium nitride film on sapphire substrate with low dielectric loss for superconducting qubits. Phys. Rev. Appl. 19, 024013. https://doi.org/10.1103/PhysRevApplied.19.024013 (2023).

Article ADS CAS Google Scholar

Vissers, M. R. et al. Low loss superconducting titanium nitride coplanar waveguide resonators. Appl. Phys. Lett. 97, 232509. https://doi.org/10.1063/1.3517252 (2010).

Article ADS CAS Google Scholar

Böhmer, A. E., Taufour, V., Straszheim, W. E., Wolf, T. & Canfield, P. C. Variation of transition temperatures and residual resistivity ratio in vapor-grown FeSe. Phys. Rev. B 94, 024526. https://doi.org/10.1103/PhysRevB.94.024526 (2016).

Article ADS CAS Google Scholar

Krishnan, M. et al. Very high residual resistivity ratios of heteroepitaxial superconducting niobium films on MgO substrates. Supercond. Sci. Technol. 24, 115002. https://doi.org/10.1088/0953-2048/24/11/115002 (2011).

Article ADS CAS Google Scholar

Russo, R., Catani, L., Cianchi, A., Tazzari, S. & Langner, J. High quality superconducting niobium films produced by an ultra-high vacuum cathodic arc. Supercond. Sci. Technol. 18, L41. https://doi.org/10.1088/0953-2048/18/7/L01 (2005).

Article ADS CAS Google Scholar

Valderrama, E. F. et al. High-RRR thin-films of NB produced using energetic condensation from a coaxial, rotating vacuum ARC plasma (CEDTM). AIP Conf. Proc. 1434, 953–960. https://doi.org/10.1063/1.4707012 (2012).

Article ADS CAS Google Scholar

Download references

K. L. X acknowledges support from the Youth Innovation Promotion Association of Chinese Academy of Sciences (2019319). J. G. F. acknowledges support from the Start-up foundation of Suzhou Institute of Nano-Tech and Nano-Bionics, CAS, Suzhou 20 (Y9AAD110).

Gusu Laboratory of Materials, Suzhou, 215123, China

Yanfu Wu, Zengqian Ding, Kanglin Xiong & Jiagui Feng

Suzhou Institute of Nano-Tech and Nano-Bionics, CAS, Suzhou, 215123, China

Kanglin Xiong & Jiagui Feng

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

Y.W.: Investigation, Data analysis, Writing – original draft. Z.D.: Investigation, Data analysis. K.X.: Project administration, Writing – review & editing. J.F.: Project administration, Conceptualization, Supervision, Writing – review & editing.

Correspondence to Kanglin Xiong or Jiagui Feng.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Wu, Y., Ding, Z., Xiong, K. et al. High-quality superconducting α-Ta film sputtered on the heated silicon substrate. Sci Rep 13, 12810 (2023). https://doi.org/10.1038/s41598-023-39420-y

Download citation

Received: 17 May 2023

Accepted: 25 July 2023

Published: 07 August 2023

DOI: https://doi.org/10.1038/s41598-023-39420-y

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative