Catalytic reductions of nitroaromatic compounds over heterogeneous catalysts with rhenium sub

Aug 18, 2023Aug 18, 2023

Scientific Reports volume 13, Article number: 12789 (2023) Cite this article

Nitroaromatic compounds (NACs) are key contaminants of anthropogenic origin and pose a severe threat to human and animal lives. Although the catalytic activities of Re nanostructures (NSs) are significantly higher than those of other heterogeneous catalysts containing NSs, few studies have been reported on the application of Re-based nanocatalysts for NAC hydrogenation. Accordingly, herein, catalytic reductions of nitrobenzene (NB), 4-nitrophenol (4-NP), 2-nitroaniline (2-NA), 4-nitroaniline (4-NA), and 2,4,6-trinitrophenol (2,4,6-TNP) over new Re-based heterogeneous catalysts were proposed. The catalytic materials were designed to enable effective syntheses and stabilisation of particularly small Re structures over them. Accordingly, catalytic hydrogenations of NACs under mild conditions were significantly enhanced by Re sub-nanostructures (Re-sub-NSs). The highest pseudo-first-order rate constants for NB, 4-NP, 2-NA, 4-NA, and 2,4,6-TNP reductions over the catalyst acquired by stabilising Re using bis(3-aminopropyl)amine (BAPA), which led to Re-sub-NSs with Re concentrations of 16.7 wt%, were 0.210, 0.130, 0.100, 0.180, and 0.090 min−1, respectively.

As nitroaromatic compounds (NACs) are key contaminants of anthropogenic origin, decomposition of these compounds has attracted significant attention1,2. NACs are carcinogenic, tumourigenic, toxic, genotoxic, or reproductive-toxic1,3,4,5,6; thus, their common occurrence in all domains of the ecosystem and various waste sources and persistent nature pose a severe threat to human and animal lives1,2,7. Therefore, considerable efforts have been made to effectively remediate NACs1,2,8,9. Catalytic reduction under mild conditions is particularly important in this regard1,2,9,10,11 as the catalytic reductions of NACs result in aromatic amines (AAMs), which are fine chemical products and serve as key building blocks for the large-scale synthesis of pharmaceuticals8,12. Thus, the development of new catalysts that increase the efficiency of NAC reduction has attracted substantial attention10,11,13,14.

In this context, catalysts based on metal nanoparticles (NPs) are important because they significantly enhance the conversions of NACs owing to their larger surface areas as compared to those of their macroequivalents10,11,13,14,15. Recently, emerging nanomaterials (NMs) based on Re nanostructures (NSs) have been recognized as attractive alternatives to previously reported NPs based on Au and Pt group metals. Re offers unique chemistry to catalytic processes mainly due to its numerous oxidation states, namely, 0 (metallic), + 3, + 4, + 6, and + 7. Compared to other metals, Re forms stable species in these oxidation states that exhibit catalytic activities in hydrogenation reactions16,17. Nevertheless, only a few studies have been reported in this regard, and the results of these studies imply that ReNSs, Re0, O-doped ReNSs, and the blends of these materials are particularly useful for homogeneous and heterogeneous catalytic reductions of NACs18,19,20,21,22. These few examples indicate that ReNSs exhibit superior catalytic activities in the reductions of NACs such as nitrobenzene (NB)21, 4-NP19,20,21,22,23,24, 2-nitroaniline (2-NA)21, 4-NA19,21,22, 2,4,-dinitrophenol, and 2,4,6-trinitrophenol (2,4,6-TNP)21.

The tendency of Re to form ultra-small NSs (< 2 nm) is one of the promising aspects of Re-based nanocatalysis19. Development of these NSs may significantly boost the catalytic activities of Re-based nanocatalysts (NCats) because of the versatile catalytic chemistries of these NSs, and a wide spectrum of catalytically active Re species could be generated, rendering Re-based NMs perfect candidates for the efficient hydrogenations of NACs. However, it is difficult to apply the smallest ReNSs as NCats and evaluate the catalytic systems in which they are used. The obstacles encountered during the development of these systems include the limited stabilities of NSs and their susceptibilities to react with atomic oxygen and reactive oxygen species21,23,24. This renders the application, access to, and design of the morphologies of ReNSs challenging16,17,19,20,21,22,23,24. These issues can be overcome using matrices in which ReNSs can be synthesised, capped, and occluded17. This strategy facilitates the stabilisation of ReNSs and hinders direct contact between Re-active sites and atmospheric O2. Nevertheless, this strategy is not entirely satisfactory as O2 dissolved in the reaction environment is sufficient to oxidise Re0NPs22, thereby decreasing the catalytic activity of the as-prepared NCat. Therefore, we proposed an alternative approach that involved preparing ReNSs as a blend of catalytically active Re species at various oxidation states24. Then, we suggested that by synthesising and capping O-doped ReNSs that could reach subnanometric sizes, the possible decreases in the catalytic activities (arising from the intended O-doping effect) of NCats could be prevented. This approach will enable the convenient use of sub-nanostructures (sub-NSs) that are usually difficult to apply and allow us to avoid the O-doping effect of Re, which may occur during the development and use of ReNS-based NCats.

Accordingly, in this study, we proposed novel heterogeneous NCats containing subnanometric (< 1 nm) ReNSs consisting of different Re species for the catalytic hydrogenations of NB, 4-NP, 2-NA, 4-NA, and 2,4,6-TNP. The developed catalytic materials demonstrated unique characteristics arising from their in situ syntheses based on an anion-exchange reaction between ReO4− and amino functionalities loaded onto polymer matrices and the capping and stabilisation of Re-active sites on these matrices. This approach is expected to effectively stabilise very small ReNSs in polymer matrices and lead to a synergistic effect between ReNSs and stabilising amino functionalities. Therefore, selected aliphatic, heterocyclic, and AAMs comprising chelating atoms, such as O and S, were used for the fabrication and capping of ReNSs. Because all Re species in ReNSs were expected to exhibit catalytic activities towards the hydrogenations of NACs17,21,22,23,24, in situ synthesis was performed in a way that allowed careful fabrication of very small ReNSs, which were blends of different O-doped ReNPs. Owing to subnanometric ReNSs and the synergistic effect between ReNSs and the polymer matrix, the resulting NCats demonstrated high catalytic activities towards the hydrogenations of NACs and better stabilities.

The new heterogenous catalysts base on polymeric matrices with stabilizing functionalities derived from bis(3-aminopropyl)amine (BAPA), 4(5)-(hydroxymethyl)imidazole (HMI), 1-(2-pyrimidyl)piperazine (PP), thiosemicarbazide (TSC), 2-amino-3-hydroxypiridine (AHP), 1-(2-hydroxyethyl)piperazine (HEP), 4(6)-aminouracil (AUr), 1,1′-carbonyldiimidazole (CDI) and 2-aminothiazol (AT). To the structure of these polymers, Re-reactive sites were introduced using two approaches, which are explained in Fig. 1. Briefly, the first approach involved the reduction of ReO4− using NaBH4 as a reducing agent (Fig. 1A), while the second approach included the reduction of ReO4− via the transfer of an electron from the N atom of the amino functionality to ReO4− (Fig. 1B). The detailed discussion on the synthesis of catalysts is provided in Supplementary Information, Sect. S1. The catalyst samples were coded using abbreviated names of amines, with the prefix extRe or Re added for the samples obtained with the external reducing agent and reduction-coupled adsorption, respectively.

Schematics of the syntheses of Re nanostructures (NSs) in the polymer matrix using (A) a reducing agent and (B) reduction-coupled adsorption and (C) structures of the amines present in anion-exchange resins.

Herein, the reduction of 4-NP to 4-aminophenol (4-AP) is chosen for modeling catalysts’ activity25. At first, the extRe samples were examined. The corresponding sets of pseudo-first-order kinetic plots and UV/Vis spectra for the catalytic reduction of 4-NP using each NCat sample are depicted in Fig. 2.

Pseudo-first-order kinetic plots and ultraviolet (UV)/visible (Vis) spectra for the reduction of 4-nitrophenol (4-NP) using catalysts containing ReNSs synthesised using an external reducing agent. Initial 4-NP concentration: 0.1 mmol L−1 and NaBH4 concentration: 0.1 mol L−1 (0.3 mL). The total reaction time and time intervals between subsequent UV/Vis spectra correspond to the data points shown in the pseudo-first-order kinetics plots.

The obtained data (Fig. 2) implied that the model catalytic reaction appropriately obeyed the pseudo-first-order kinetics as correlation coefficients (R2) ranged from 0.83 to 1 (Fig. 2). The fabricated NCat samples were divided into two groups. The first group of samples comprised extReBAPA, extReCDI, extReHMI, extReAHP, and extReHEP and demonstrated catalytic activities for the reduction of 4-NP to 4-AP. The highest pseudo-first-order rate constant (k1) (5.17 × 10−2 min−1) was observed in the case of extReHEP, whereas the smallest k1 was observed for extReAHP (9.01 × 10−4 min−1). This simultaneously influenced the 4-NP conversion yield (%). extReHEP led to > 95% conversion of 4-NP within 300 min, whereas extReCDI (k1 = 2.33 × 10−3 min−1) and extReHMI (k1 = 1.64 × 10−2 min−1) resulted in 95 and 93% conversions of 4-NP within 125 and 175 min, respectively. extReAHP was considerably less efficient as it led to only 27% conversion of 4-NP with k1 = 9.01 × 10−4 min−1. The second group of samples consisting of extRePP, extReTSC, extReAUr, and extReAT exhibited insufficient catalytic activities for the reduction of 4-NP to 4-AP. The k1 values obtained for the second group of samples were approximately one order of magnitude lower than those achieved for the first group of samples and ranged from 4.84 × 10−5 to 9.61 × 10−5 min−1. Furthermore, negligible catalytic conversions of 4-NP (< 4%) were acquired using the second group of samples.

Adsorption of ReO4− on anion-exchange resins more efficiently proceeds on amines with complex structures26,27,28. In this context, Certainly, there is a relationship between the observed catalytic activities of NCats and the structures of the amines incorporated into the polymer matrices of NCats (Fig. 1C). Samples containing amines with complex structures, namely, a clam-like structure (CDI), samples comprising substituents based on an aliphatic chain (HMI and HEP), or samples characterised by a long-chain aliphatic structure (BAPA) demonstrated significantly higher catalytic activities as compared to those of the samples containing short substituents (PP, TSC, AHP, AUr, and AT) (Fig. 1C). This indicated that the functionalities derived from CDI, HMI, HEP, and BAPA might provide a synergistic effect between the polymer matrix and the ReNSs, and thus, NCats with high catalytic activities would be obtained. This synergistic effect may not be the only reason for the differences observed between the apparent k of the catalytic reductions of 4-NP to 4-AP performed using different NCats. Several other factors, including the concentration of Re in the samples, average sizes of the fabricated ReNSs, and the oxidation state of Re in the synthesised ReNSs, might also influence the catalytic activities of NCats. The effects of these factors on the catalytic activities of NCats are discussed later in the manuscript.

The catalytic activities of the samples obtained using second synthesis approach (Fig. 1B) were also analysed for the model reduction reaction, and the corresponding results are shown in Fig. 3. The highest catalytic activity was observed in the case of ReBAPA, which converted 97% 4-NP within 40 min with k1 = 0.012–0.21 min−1 (Fig. 3). The same 4-NP conversion yield was achieved within 47 min using ReHMI. However, in this case, k1 was 0.077 min−1. The remaining samples ReCDI, ReHEP, and ReAHP resulted in 97, 83, and 32% 4-NP conversions with k1 values of 0.064, 0.61 × 10−3, and 0.27–4.1 × 10−2 min−1, respectively. These data are consistent with the results obtained for the catalysts comprising extRe as the apparent catalytic activities of ReBAPA, ReCDI, ReHMI, ReHEP, and ReAHP (the first group of samples) are linked with the functionalities derived from BAPA, CDI, HMI, HEP, and AHP, respectively. RePP, ReTSC, ReAUr, and ReAT (the second group of samples) exhibited negligible or no catalytic activities for this reaction, similar to the cases of their equivalents acquired using NaBH4 (Figs. 2 and 3). This suggested that the conclusion regarding the synergistic effect between amino functionalities and ReNSs was valid.

Pseudo-first-order kinetic plots and UV/Vis spectra for the reductions of 4-NP using different catalysts containing Re-active sites fabricated by reduction-coupled adsorption of ReO4− on amino functionalities. Initial 4-NP concentration: 0.1 mmol L−1 and NaBH4 concentration: 0.1 mol L−1 (0.3 mL). The total reaction time and time intervals between subsequent UV/Vis spectra correspond to the data points depicted in the pseudo-first-order kinetic plots.

To make comparing the data easier, Table S4 located in the Supplementary Information, Sect. S1.4 sets obtained rate constants, together with Turnover Frequencies (TOF) and maximum yields of NACs conversions for all of the samples. Based on Figs. 2 and 3 and Table S4 significant differences were observed between the catalytic activities of the NCat samples obtained using the two methods (Fig. 1A,B). Generally, the catalytic activities of the Re samples were substantially higher than those of the extRe samples. For instance, the k1 value calculated for ReBAPA (0.21 min−1) was an order of magnitude higher than the corresponding value evaluated for extReBAPA (1.78 × 10−3 min−1). Similar phenomena were noticed for ReCDI and extReCDI (k1 = 0.064 vs. 2.33 × 10−3 min−1), ReHIM and extReHIM (k1 = 0.077 vs. 1.64 × 10−2 min−1), and ReHEP and extReHEP (k1 = 0.041 vs. 3.25 × 10−2 min−1), respectively. These observations, combined with received TOF parameters (Table S4) suggest that this tendency is associated with the method applied for the syntheses of NCats. Thus, the origin of this tendency can be hypothesised to be the differences between the physiochemistries of ReO4− reductions conducted by different methods. This could further influence the final morphologies of the NSs produced. It was speculated that the ReNSs formed using reduction-coupled adsorption might be considerably smaller and better dispersed than those constructed using NaBH429,30. This could be the reason for the higher catalytic activities of the Re samples than those of the extRe samples. Therefore, the above-mentioned issue is comprehensively discussed in the next section.

First, it was verified, whether the differences in the observed catalytic activities might have been caused by unequal concentrations of Re in the synthesized samples. The determined concentration of Re and detailed discussion is provided in Supplementary Information, Sect. S1.2 and Table S2. Briefly, the concentrations of Re in the Re samples were higher than those in the extRe samples. This explains why the Re samples demonstrated significantly higher catalytic activities than the extRe samples (Figs. 2 and 3). Further, the NCats demonstrated different concentrations of Re, ranging from 0 to 7.1% in the cases of the extRe samples and from 0 to 18.4% in the cases of the Re samples (Table S2). Among all the applied amines, AUr and TSC evidently prevented or suppressed the reduction of Re(VII) (CRe values for these samples were ~ 0%, Table S2). Additionally, despite relatively high Re concentrations of extRePP, RePP, extReAT, and ReAT (7.1, 17.0, 4.6, and 12.5%, respectively), these NCats exhibited negligible catalytic activities (Figs. 2 and 3); in contrast, other NCats with similar Re concentrations (for example, extReHEP and ReHEP, Table S2) demonstrated outstanding catalytic activities. These observations confirm the synergistic effect between ReNSs and amino functionalities and allow us to conclude that the applied amine precisely regulates the synthesis routes of ReNSs irrespective of the method used.

Second, despite differences in Re concentrations, it was verified how amines, and the methods of syntheses influenced the morphology of the ReNSs. At first, the morphologies of the polymer samples were assessed via ultra-high resolution scanning electron microscopy (UHR-SEM); additional assessments of the polymer cross-sections (achieved using Ga-focused ion beam (FIB) and Xe-plasma FIB) and elemental mapping acquired using energy dispersive X-Ray spectrometer (EDX) were also performed. Figure 4 shows the SEM and UHR-SEM images of the representative samples ReBAPA, extReBAPA, and extRePP. These samples were chosen because of the following reasons. The findings obtained for ReBAPA and extReBAPA may explain why the two different methods of ReNS syntheses resulted in significantly different Re concentrations in the NCats. Moreover, combining these observations with those acquired for extRePP may clarify why extRePP exhibits negligible catalytic activity despite its higher Re concentration (Table S2) and why extReBAPA outperforms it.

Ultra-high-resolution scanning electron microscopy images of (A) ReBAPA, (B) extReBAPA, and (C) extRePP. (1) Morphologies of nanocatalyst (NCat) grains, (2) Morphologies of the NCat surfaces, (3) Focussed ion beam cross-sections, and (4) Energy-dispersive X-ray (EDX) maps of the cross-sections (towards Re).

extRePP is covered with a large number of agglomerates derived from Re (as indicated by the EDX map) (Fig. 4C1). Although a closer observation (Fig. 4A2,B2, and C2) revealed the presence of ReNS agglomerates on the surfaces of all samples, the surfaces of ReBAPA and extReBAPA had considerably less agglomerates. Observations of the polymer cross-sections revealed another phenomenon. The areas below the surfaces of the polymer grains were almost entirely clear in the cases of ReBAPA and extReBAPA (Fig. 4A3,B3, respectively), whereas those in the case of extRePP comprised large particles and their agglomerates (Fig. 4C3). Simultaneously, the EDX mapping of Re on the cross-sections demonstrated that ReBAPA had a uniform distribution of Re from the surface to the centre of the polymer grain (Fig. 4A4), while within extReBAPA (Fig. 4B4) the higher density of Re was observed in close proximity to the extReBAPA surface. The absence of particles in the cross-sections of ReBAPA and extReBAPA (Fig. 4A3,B3) implied that Re produced very small NSs, and UHR-SEM was unable to observe them. Thus, high-resolution transmission electron microscopy analysis (HRTEM) was conducted. Figure 5 depicts the HRTEM images of the cross-sections of ReBAPA, extReBAPA, and extRePP as the representative samples.

High- resolution transmission electron microscopy images, selected area electron diffraction patterns, and EDX spectra of (A) ReBAPA, (B) extReBAPA, and (C) extRePP.

The observation of the NCat samples was difficult, even using HRTEM. The images of extRePP demonstrated some structures near the polymer grain surface (first panel) and in the inner part of the polymer grain (right panel) (Fig. 5C). According to the EDX spectra (Fig. 5), all these structures were based on Re. The particles situated near the polymer grain surface were bigger (sizes: ~ 2–10 nm), whereas the particles in the inner part of the polymer grain were smaller (sizes: 0.83 ± 0.52 nm, dark spots in Fig. 5C, right panel). The same phenomenon was observed for extReBAPA (Fig. 5B). Nevertheless, in this case, the number of NSs was considerably lower than that of extRePP (Fig. 5B,C). The difference between the observed catalytic activities of extReBAPA and extRePP led to further uncertainties as extReBAPA outperformed extRePP in the catalytic reduction of 4-NP (Fig. 2). This suggested the primary role of BAPA in the syntheses and performances of NCats; however, a possible reason for this phenomenon could be deduced by investigating both samples containing BAPA functionalities (extReBAPA, ReBAPA). extReBAPA comprised a small number of NSs, whereas ReBAPA contained no NSs (Fig. 5A). Some phase contrast was noticed near the polymer grain surface in Fig. 5A, which indicated the production of very small structures; nevertheless, HRTEM was not a suitable technique to examine these structures. The significantly high catalytic activity of ReBAPA than those of all other NCats further validates the hypothesis that some Re-based structures must have formed in ReBAPA (Figs. 2 and 3). This finding necessitates further investigation of ReBAPA. Thus, additionally, HRTEM in the scanning-transmission (STEM) mode using large magnifications and a high angle annular dark field detector (HAADF) was performed. Figure 6 shows the corresponding images.

Scanning transmission electron microscopy images of (A) ReBAPA, (B) extReBAPA, and (C) extRePP.

Large magnifications, along with the use of the STEM-HAADF mode, allowed the observation of single Re atoms (bright spots in the images depicted in Fig. 6). These atoms occasionally grouped in sub-NSs, implied by the local increase in Re density (larger bright areas). Single NSs were observed for extReBAPA and extRePP (Figs. 5B,C and 6B,C, left panels), whereas the situation was completely different in the case of ReBAPA, which consists of large areas entirely loaded with Re atoms that tended to group on the << 1 nm scale were noticed (Fig. 6A, right panel). The corresponding images might have been acquired at the very beginning of the formation of these structures, which would have been “frozen” by the polymer matrix itself. This was ascribed to the effective stabilisation of ReO4− by amines, which might have prevented the growth of reduced Re forms. According to these findings, it was concluded that although BAPA prevented the formation of NSs, it facilitated the production of Re-sub-NSs, which were catalytically active and substantially boosted the catalytic activities of catalysts in the reduction of 4-NP. This conclusion might be extended to other samples that exhibited higher catalytic activities than those of other samples. Thus, CDI, HMI, and HEP functionalities must also contribute to the formation of Re-sub-NSs.

The selected area energy diffraction (SAED) patterns obtained during HRTEM (Fig. 5) indicated amorphous morphologies of the investigated materials. These observations could indicate the existence of Re–Re bonds in ReNSs21,31,32. Nevertheless, Re can form various stable species16,17, and the Re-sub-NSs observed by STEM-HAADF exhibited amplitude contrasts originating from the lack of long-range orderings of the particles. Therefore, SAED was not sufficient to draw any binding conclusions in this case. Therefore, X-Ray photoelectron spectroscopy (XPS) analysis was performed to determine the types of Re species in the synthesized samples.

Surface concentrations of chemical bonds achieved by fitting the XPS data for all analyzed samples are presented in Table S3. Furthermore, the methodology for determining specific bonds is systematically described in Sect. S2 of the supplementary information. Moreover, all the acquired spectra are provided in S3.1 (survey scans) and S3.2 (high-resolution spectra). Re 4f spectra (Section S1.2) were fitted with up to three doublet structures (doublet separation f7/2–f5/2 = 2.43 eV) with the first 4f7/2 line centred at 42.4 eV, which implied the presence of Re4+ similar to that in ReO2. The second 4f7/2 line centred at 44.0 eV demonstrated the existence of Re6+ similar to that in ReO3, and the last 4f7/2 line at 46.1 eV indicated the presence of Re7+ similar to that in Re2O733,34. Based on these results, it was concluded that the reduction of ReO4− was indeed successful. Additionally, note that Re7+ in Re2O7 was different from Re7+ in NH4ReO4 (precursor).

Atomic% Re concentrations provided in Table S3 are consistent with those determined in Table S2. Generally, the concentrations of Re in extRe samples were lower than those in the Re samples. Moreover, the atomic% concentrations of Re4+, Re6+, and Re7+ were typically higher in the second group of samples (Table S3). All these findings agreed with the observed k values of 4-NP reduction for the Re samples; as evidenced in the model reaction, the Re samples outperformed the extRe samples (Figs. 2 and 3).

ReBAPA, ReCDI, ReHMI, ReHEP, extReBAPA, extReCIM, extReHMI, and extReHEP efficiently reduced ReO4− as Re4+, Re6+, and Re7+ in the form of Re2O7 were present in these samples. However, RePP, ReTSC, ReAHP, ReAT, extRePP, extReTSC, extReAHP, and extReAT also contained these forms of Re and exhibited inferior or no catalytic activities. This phenomenon can be explained by comparing the data provided in Tables S2 and S3. Based on the XPS results, the atomic% Re concentrations of extRePP and extReTSC, which were not catalytically active, were higher than that of extReBAPA, which outperformed extRePP and extReTSC in the catalytic reduction of 4-NP. Hence, the following conclusions can be drawn: First, Re in the extRe samples is generally concentrated near the polymer grain surface. Second, according to the atomic% Re concentrations (Table S3), it can be specified that the same phenomenon (namely, the location of Re on the sample surface) is induced by the application of PP, TSC, AHP, and AT; the samples obtained using these amines contain more Re atoms on their surfaces than those in the cases of other catalytically active samples (Table S3). These results are consistent with the UHR-SEM, HRTEM, and EDX results. This indicated that the application of BAPA, CDI, HMI, and HEP typically resulted in the formation of several Re species in the whole volume of the sample, and therefore, the production of Re-sub-NSs in the inner part of the polymer grain was possible. This further confirmed the abovementioned synergistic effect between ReNSs and amino functionalities, which was the key to achieving high catalytic activities.

The results of catalytic activity analysis and the assessments of the characteristics of ReNSs and Re-sub-NSs implied a direct relationship among the amines present in the polymer matrix, properties of Re, and catalytic activities of the synthesised NCats. Although all the NCat samples containing functionalities derived from BAPA, CDI, HMI, and HEP were effective for the hydrogenation of 4-NP to 4-AP, ReBAPA outperformed all other NCats, leading to > 95% conversion of 4-NP in just 15 min with a k1 of 0.21 min−1 (Fig. 3). Therefore, ReBAPA was chosen for further analyses. Figure 7 depicts the first-order kinetic plots acquired for the reductions of NB, 2-NA, 4-NA, and 2,4,6-TNP using ReBAPA and the UV/Vis spectra for each reduction.

Reductions of NB, 2-NA, 4-NA, and 2,4,6-TNP using ReBAPA. Initial concentration of the nitroaromatic compound (NAC): 0.1 mmol L−1 and NaBH4 concentration: 0.1 mol L−1 (0.3 mL). The total reaction time and time intervals between subsequent UV/Vis spectra correspond to the data points presented in the first-order kinetic plots.

The obtained spectra demonstrated that ReBAPA enabled the reduction of NB to aniline35, the reduction of 4-NA to 1,4-diaminobenzene36, and the reductions of 2-NA37 and 2,4,6-TNP38. Although the highest k1 was acquired for the model 4-NP reduction, the k1 values of the catalytic processes performed using other NACs ranged from 0.09 to 0.18 min−1. As these differences were not considerable, these might have originated from the reaction itself rather than from the different catalytic activities of ReBAPA for different NACs. For instance, the km values calculated for the reductions of 4-NP and 2,4,6-TNP were 4.77 and 1.67 g−1 min−1, respectively. This almost three-fold difference between the km values for 4-NP and 2,4,6-TNP was proportional to the number of –NO2 groups present in the structures of 4-NP (one group) and 2,4,6-TNP (three groups). Nevertheless, this observation did not explain why the catalytic activity of ReBAPA was slightly lower for 2,4,6-TNP than those in the cases of other NACs. Consequently, the yields (%) of NAC reductions, along with the TOF values at 20, 50, 70, and 80% NAC reduction, were examined and detailed in Supplementary Information, Sect. S1 and Fig. S1. Based on these, it might be suggested that ReBAPA revealed similar catalytic activity towards each NAC (the detailed discussion is provided in Supplementary Information, Sect. S1.4).

Up to date, few studies have been reported on the application of homogeneous and heterogeneous Re-based NCats in the hydrogenations of NACs, which are summarised in Table 1. The results of this study confirmed that the heterogeneous NCat ReBAPP developed herein was more efficient than the homogeneous catalysts based on Re nanoclusters19 and raw ReNSs23. Additionally, the calculated k1 values were similar to those obtained using hybrid catalysts comprising Ag and AuNPs anchored on ReS2 nanosheets31. Nevertheless, ReBAPP also outperformed PtNPs immobilised on ReS2 in the reductions of 4-NP and 2-NA31. Although homogeneous NCats based on Re are rare, heterogeneous NCats based on Re are even rarer. When this manuscript was written (July 2023), a review of the literature revealed that few studies were reported on the application of Re-based heterogeneous NCats in the hydrogenations of NACs. In our previous studies, we attempted to optimise the structures of ReNSs by synthesising Re-based NMs with Re022 or O-doped ReNSs24. Although the first approach resulted in Re0NPs with high catalytic activities, it did not offer catalyst stability as the Re0NPs interacted with O and thus lost their catalytic activities22. In contrast, the other approach based on reduction-coupled adsorption enabled the fabrication of O-doped ReNSs with slightly lower catalytic activities and higher stabilities than those of the abovementioned Re0NPs in the catalytic reduction of 4-NP24.

In this study, we propose unique NCats loaded with ReNSs and Re-sub-NSs that can efficiently reduce NACs under mild conditions. The findings herein revealed that the unique reduction-coupled adsorption of ReO4− on amino functionalities should be preferred for the fabrication of ReNSs rather than the approach involving the use of an external reducing agent. Reduction-coupled adsorption eliminates the application of toxic reducing agents and leads to NCats with Re-sub-NSs, which significantly boost the catalytic activities of heterogeneous catalysts.

Results indicated a synergistic effect between the ReNSs and the amino functionalities present in the polymer matrix. The amino functionalities with complex structures enabled efficient stabilisation of Re atoms, resulting in Re-sub-NSs. Moreover, a synergistic effect was noticed between NCats and the amines applied for their stabilisation. The amino functionalities with complex structures provided high catalytic activities to NCats. The mechanism of ReO4− reduction was simple and did not require additional preparation or strict control over the synthesis conditions. Consequently, ReO4− present in the polymer matrix formed Re4+, Re6+, and Re7+ O-doped species, which exhibited outstanding catalytic activities when combined with a synergistic amine. The type of Re species generated did not influence the catalytic activities of NCats as the corresponding ReNSs and Re-sub-NSs were versatile. In this regard, the kind of amine was the only limiting factor affecting the catalytic activities of NCats. Using a selected amine, the sizes of the structures formed by Re can be regulated, facilitating the development of NCats with high catalytic activities.

This study provides further insight into these unique NMs. First, Re-based NCats can be applied to other reductions instead of only the model reaction as this type of NCats effectively reduce other NACs in addition to 4-NP. Second, because of the versatility of ReNSs, the forms in which Re-based NPs are produced do not influence the catalytic activities of NCats, and thus, ReNSs can be prepared via simpler procedures. Third, the application of an appropriate amine enables the formation of Re subnanometric structures that further boost the catalytic activities of Re-based materials. Fourth, owing to the synergistic effect between ReNSs and amino functionalities and the affinity of the polymer matrix to NACs, the catalytic activities of the developed NCats can be enhanced or tailored. Thus, based on the results of this study, a process for NAC reduction that can be performed in a flow mode with the simultaneous production of AAMs can be envisioned.

Detailed list of standard materials, instrumentation, and synthetic protocols is provided in Supplementary Information, Sect. S1.

For the synthesis of polymeric base (anion exchange resins) the following materials were used: vinylbenzyl chloride (VBC), divinylbenzene (DVB), benzoyl peroxide, poly(vinyl alcohol), bis(3-aminopropyl)amine (BAPA), 4(5)-(hydroxymethyl)imidazole (HMI), 1-(2-pyrimidyl)piperazine (PP), thiosemicarbazide (TSC), 2-amino-3-hydroxypiridine (AHP), 1-(2-hydroxyethyl)piperazine (HEP), 4(6)-aminouracil (AUr), 1,1′-carbonyldiimidazole (CDI) and 2-aminothiazol (AT). The loading of ReNSs, the ammonium perrhenate (NH4ReO4) was used. For the catalytic studies selected NACs, that is, NB, 4-NP, 2-NA, 4-NA, and 2,4,6-TNP, together with NaBH4 were used.

The concentration of N (ZN) derived from amino functionalities was determined by elemental analysis using. Morphologies of the polymer samples were assessed by ultra-high-resolution scanning electron microscopy (UHR-SEM) aided by Ga-focused ion beam (Ga-FIB) and Xe-PFIB and energy-dispersive X-ray (EDX) spectrometers. Moreover, ReNSs loaded onto different polymers were characterised by high-resolution transmission electron microscopy (HRTEM) aided by a selected area electron diffractometer, EDX spectrometer, and high-angle annular dark-field (HAADF) detector in the scanning transmission electron microscopy (STEM) mode. Concentrations of Re in the NCat samples were determined via inductively coupled plasma optical emission spectrometry (ICP-OES). Before analysis, the ReNS-loaded polymer samples were washed with a 1% NH4OH solution to remove unreduced ReO4−. The Re oxidation states were determined using X-ray photoelectron spectroscopy (XPS) by obtaining high-energy resolution spectra for Re 4f region. The catalytic reaction rate was monitored by ultraviolet/visible (UV/Vis) spectrophotometry. The reaction rates were determined using the corresponding UV/Vis spectra by calculating the maximum absorbance of NACs at a specific wavelength (λmax). For the reaction, 2.5 mL of a NAC solution (0.1 mmol L−1) was added to a 3 mL quartz cuvette. Subsequently, 0.3 mL NaBH4 solution (0.1 mol L−1) was introduced, and the absorbance at λmax = 400, 275, 410, 380, 390 nm was measured for 4-NP, NB, 2-NA, 4-NA, and 2,4,6-TNP, respectively. Based on the decrease of absorbance, − ln(At/A0) versus t plots were constructed (where At is the absorbance at time t and A0 is the absorbance at the beginning of the process), and rate constants (k (min−1)) were evaluated from the slopes of these plots. Next, the k values were recalculated to obtain the mass-normalised rate constants km (g−1 min−1). Finally, the mass-dependent activity of each catalyst was estimated using turnover frequency (TOF, min−1), defined as n4-NP × r × nRe−1 × t−1, where n4-NP and nRe represent the number of moles of 4-NP and ReNSs at the start of the process, respectively, t is the process time (min), and r is the yield (%) of reduction at which TOF is calculated.

At first, the polymer matrix, namely, VBC-co-DVB (copolymer), was fabricated by suspension polymerisation. Then, the resultant copolymer VBC-co-DVB was separately modified by selected amines, that is, BAPA, 1,1′-carbonyldiimidazole (CDI), HMI, PP, TSC, AHP, HEP, AUr, and AT. Subsequently, the resulting anion-exchange resins (0.1 g) were mixed with solutions (50 mL, 500 mg Re L−1) containing NH4ReO4 in 0.1 mol L−1 HCl. This led to anion exchange between amino functionalities and ReO4−. Thereafter, two approaches were used to synthesise and stabilise ReNSs in the polymer matrix (Fig. 1).

The first approach involved the reduction of ReO4− using NaBH4 as a reducing agent. Typically, the Re(VII)-loaded anion-exchange resins were separated from the precursor solution by filtration and washed with water on a fritted-glass funnel followed by introduction into 50 mL water comprising 0.1 mol L−1 NaBH4. This resulted in the immediate syntheses and precipitations of ReNSs in the polymer matrix. After 24 h, each resin was separated by filtration, washed with water, and used in its swollen state. The second approach included the reduction of ReO4− via the transfer of an electron from the N atom of the amino functionality to ReO4− (Fig. 1B). Subsequently, the Re(VII)-loaded anion-exchange resins were separated from the precursor solution, washed with water, and stored in 50 mL water for 4 weeks. This caused gradual reduction and precipitation of ReNSs. Although both methods involved in situ reduction, the second method provided a stable concentration gradient between the reactive groups (amino functionalities) and ReO4− at the solid/liquid interface without any external reducing agent; thus, the resulting ReNSs were expected to be smaller and appropriately dispersed in the polymer matrix as compared to the cases of NMs achieved using NaBH4.

NCat samples were named according to the abbreviations of the amines present in the prepared polymer matrices, and the prefixes extRe and Re were used to represent ReNSs obtained using an external reducing agent (for example, extReBAPA) and reduction-coupled adsorption (for instance, ReBAPA), respectively.

All data generated or analysed during this study are included in this published article and its supplementary information.

Tiwari, J., Tarale, P., Sivanesan, S. & Bafana, A. Environmental persistence, hazard, and mitigation challenges of nitroaromatic compounds. Environ. Sci. Pollut. Res. 26, 28650–28667 (2019).

Article CAS Google Scholar

Bilal, M., Bagheri, A. R., Bhatt, P. & Chen, S. Environmental occurrence, toxicity concerns, and remediation of recalcitrant nitroaromatic compounds. J. Environ. Manag. 291, 112685 (2021).

Article CAS Google Scholar

Smith, G. F. Progress in Medicinal Chemistry Vol. 50, 1–47 (Elsevier, 2011).

Google Scholar

Urben, P. G. Bretherick’s Handbook of Reactive Chemical Hazards 7th edn, 65–133 (Academic Press, 2007).

Google Scholar

Electronic document: https://www.epa.gov/sites/production/files/2016-09/documents/4-nitrophenol.pdf. Access Date: 21 Jan 2019.

Benbrahim-Tallaa, L. et al. (Elsevier, 2012).

Keyte, I. J., Albinet, A. & Harrison, R. M. On-road traffic emissions of polycyclic aromatic hydrocarbons and their oxy-and nitro-derivative compounds measured in road tunnel environments. Sci. Total Environ. 566, 1131–1142 (2016).

Article ADS PubMed Google Scholar

Kadam, H. K. & Tilve, S. G. Advancement in methodologies for reduction of nitroarenes. RSC Adv. 5, 83391–83407 (2015).

Article ADS CAS Google Scholar

Ju, K.-S. & Parales, R. E. Nitroaromatic compounds, from synthesis to biodegradation. Microbiol. Mol. Biol. Rev. 74, 250–272 (2010).

Article CAS PubMed PubMed Central Google Scholar

Din, M. I. et al. Critical review on the chemical reduction of nitroaniline. RSC Adv. 10, 19041–19058 (2020).

Article ADS CAS PubMed PubMed Central Google Scholar

Zhang, K. et al. Recent advances in the nanocatalyst-assisted NaBH4 reduction of nitroaromatics in water. ACS Omega 4, 483–495 (2019).

Article CAS PubMed PubMed Central Google Scholar

Provenzani, A. & Polidori, P. Covid-19 and drug therapy, what we learned. Int. J. Clin. Pharm. 42, 1 (2020).

Article Google Scholar

Nandi, S., Patel, P., Noor-ul, H. K., Biradar, A. V. & Kureshy, R. I. Nitrogen-rich graphitic-carbon stabilized cobalt nanoparticles for chemoselective hydrogenation of nitroarenes at milder conditions. Inorg. Chem. Front. 5, 806–813 (2018).

Article CAS Google Scholar

Qin, L. et al. Synthetic strategies and application of gold-based nanocatalysts for nitroaromatics reduction. Sci. Total Environ. 652, 93–116 (2019).

Article ADS PubMed Google Scholar

Eskandarinezhad, S., Khosravi, R., Amarzadeh, M., Mondal, P. & Magalhães Filho, F. J. C. Application of different nanocatalysts in industrial effluent treatment: A review. J. Compos. Compd. 3, 43–56 (2021).

Google Scholar

Davenport, W. H., Kollonitsch, V. & Klein, C. H. Advances in rhenium catalysts. Ind. Eng. Chem. 60, 10–19 (1968).

Article CAS Google Scholar

Gothe, M. L. et al. Rhenium–A tuneable player in tailored hydrogenation catalysis. Eur. J. Inorg. Chem. 2021, 4043–4065 (2021).

Article CAS Google Scholar

Kundu, S. et al. Polymer encapsulated self-assemblies of ultrasmall rhenium nanoparticles: Catalysis and SERS applications. ACS Sustain. Chem. Eng. 5, 10186–10198 (2017).

Article CAS Google Scholar

Anantharaj, S. et al. Ultra-small rhenium nanoparticles immobilized on DNA scaffolds: An excellent material for surface enhanced Raman scattering and catalysis studies. J. Colloid Interface Sci. 483, 360–373 (2016).

Article ADS CAS PubMed Google Scholar

Ribeiro, A. P., Santos, B. M., Faustino, R. F., Pombeiro, A. J. & Martins, L. M. C-heterogenized Re nanoparticles as effective catalysts for the reduction of 4-nitrophenol and oxidation of 1-phenylethanol. Catalysts 12, 285 (2022).

Article CAS Google Scholar

Veerakumar, P., Thanasekaran, P., Lin, K.-C. & Liu, S.-B. Well-dispersed rhenium nanoparticles on three-dimensional carbon nanostructures: Efficient catalysts for the reduction of aromatic nitro compounds. J. Colloid Interface Sci. 506, 271–282 (2017).

Article ADS CAS PubMed Google Scholar

Cyganowski, P., Dzimitrowicz, A., Jamroz, P., Jermakowicz-Bartkowiak, D. & Pohl, P. Rhenium nanostructures loaded into amino-functionalized resin as a nanocomposite catalyst for hydrogenation of 4-nitrophenol and 4-nitroaniline. Polymers 13, 3796 (2021).

Article CAS PubMed PubMed Central Google Scholar

Cyganowski, P., Terefinko, D., Jamroz, P., Pohl, P. & Dzimitrowicz, A. Non-thermal atmospheric pressure plasma as a powerful tool for the synthesis of rhenium-based nanostructures for the catalytic hydrogenation of 4-nitrophenol. RSC Adv. 11, 38596–38604 (2021).

Article ADS CAS PubMed PubMed Central Google Scholar

Cyganowski, P. & Dzimitrowicz, A. Heterogenous nanocomposite catalysts with rhenium nanostructures for the catalytic reduction of 4-nitrophenol. Sci. Rep. 12, 1–12 (2022).

Article Google Scholar

Strachan, J., Barnett, C., Masters, A. F. & Maschmeyer, T. 4-Nitrophenol reduction: Probing the putative mechanism of the model reaction. ACS Catal. 10, 5516–5521 (2020).

Article CAS Google Scholar

Cyganowski, P., Cierlik, A., Leśniewicz, A., Pohl, P. & Jermakowicz-Bartkowiak, D. Separation of Re (VII) from Mo (VI) by anion exchange resins synthesized using microwave heat. Hydrometallurgy 185, 12–22 (2019).

Article CAS Google Scholar

Virolainen, S., Laatikainen, M. & Sainio, T. Ion exchange recovery of rhenium from industrially relevant sulfate solutions: Single column separations and modeling. Hydrometallurgy 158, 74–82 (2015).

Article CAS Google Scholar

Jia, M. et al. Adsorption and separation of rhenium(VII) using N-methylimidazolium functionalized strong basic anion exchange resin. J. Chem. Technol. Biotechnol. 88, 437–443 (2013).

Article ADS CAS Google Scholar

Cyganowski, P. et al. Molecular reactors for synthesis of polymeric nanocomposites with noble metal nanoparticles for catalytic decomposition of 4-nitrophenol. J. Colloid Interface Sci. 541, 226–233 (2019).

Article ADS CAS PubMed Google Scholar

Cyganowski, P., Jermakowicz-Bartkowiak, D., Leśniewicz, A., Pohl, P. & Dzimitrowicz, A. Highly efficient and convenient nanocomposite catalysts produced using in-situ approach for decomposition of 4-nitrophenol. Colloids Surf. A Physicochem. Eng. Asp. 590, 124452 (2020).

Article CAS Google Scholar

Dhenadhayalan, N., Lin, T. W., Veerakumar, P. & Lin, K. C. Metal nanoparticles anchored on rhenium disulfide nanosheets as catalysts for the reduction of aromatic nitro compounds. ChemNanoMat 4, 1262–1269 (2018).

Article CAS Google Scholar

Cyganowski, P. et al. The use of cold atmospheric pressure plasma for the synthesis of saccharide-stabilized Re nanostructures enabling effective deactivation of nitro-based antimicrobial agents. Plasma Chem. Plasma Process. 43, 199–224 (2023).

Article CAS Google Scholar

Wagner, C. D. et al. (Version, 2003).

Okal, J., Tylus, W. & Kȩpiński, L. XPS study of oxidation of rhenium metal on γ-Al2O3 support. J. Catal. 225, 498–509 (2004).

Article CAS Google Scholar

Murugan, E., Rangasamy, R. & Pakrudheen, I. Efficient amphiphilic poly (propyleneimine) dendrimer stabilized gold nanoparticle catalysts for aqueous phase reduction of nitrobenzene. Sci. Adv. Mater. 4, 1103–1110 (2012).

Article CAS Google Scholar

Jakhmola, A. et al. Self-assembly of gold nanowire networks into gold foams: Production, ultrastructure and applications. Inorg. Chem. Front. 4, 1033–1041 (2017).

Article CAS Google Scholar

Naeem, H., Ajmal, M., Muntha, S., Ambreen, J. & Siddiq, M. Synthesis and characterization of graphene oxide sheets integrated with gold nanoparticles and their applications to adsorptive removal and catalytic reduction of water contaminants. RSC Adv. 8, 3599–3610 (2018).

Article ADS CAS PubMed PubMed Central Google Scholar

Sarmah, K., Pal, J., Maji, T. K. & Pratihar, S. Magnetically recoverable heterobimetallic Co2Mn3O8: Selective and sustainable oxidation and reduction reactions. ACS Sustain. Chem. Eng. 5, 11504–11515 (2017).

Article CAS Google Scholar

Download references

This work was financed by the funds received from the National Science Centre (Poland) as part of the research project UMO-2020/39/D/ST8/01352 granted to Piotr Cyganowski. This study was also supported by the subsidy granted to the Wroclaw University of Science and Technology from the funds of the Polish Ministry of Education and Science. Piotr Cyganowski and Anna Dzimitrowicz were provided by the scholarship for outstanding young scientists within the programme of Polish Ministry of Education and Science.

Department of Process Engineering and Technology of Polymer and Carbon Materials, Faculty of Chemistry, Wroclaw University of Science and Technology, Wybrzeze S. Wyspianskiego 27, 50-370, Wrocław, Poland

Piotr Cyganowski & Dorota Jermakowicz-Bartkowiak

Department of Analytical Chemistry and Chemical Metallurgy, Faculty of Chemistry, Wroclaw University of Science and Technology, Wybrzeze S. Wyspianskiego 27, 50-370, Wrocław, Poland

Anna Dzimitrowicz, Anna Lesniewicz & Pawel Pohl

Academic Centre for Materials and Nanotechnology, AGH University of Science and Technology, A. Mickiewicza Av. 30, 30-059, Kraków, Poland

Mateusz M. Marzec, Krystian Sokołowski & Andrzej Bernasik

Łukasiewicz Research Network - PORT Polish Center for Technology Development, Stablowicka 147, 54-066, Wrocław, Poland

Sebastian Arabasz

Laboratory of Microscopic Techniques, Faculty of Biological Sciences, University of Wroclaw, H. Sienkiewicza 21, 50-335, Wrocław, Poland

Sylwia Nowak

Faculty of Physics and Applied Computer Science, AGH University of Science and Technology, A. Mickiewicza Av. 30, 30-059, Kraków, Poland

Andrzej Bernasik

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

P.C.: conceptualization, methodology, validation, formal analysis, investigation, resources, data curation, writing-original draft, visualisation, supervision, project administration, funding acquisition. A.D.: investigation, resources, writing-review and editing. M.M.M. and K.S.: methodology, validation, investigation, data curation, writing-review and editing. S.A., S.N. and A.L.: investigation. P.P.: methodology, validation, formal analysis, investigation, writing-review and editing. A.B. and D.J.B.: resources, writing-review and editing.

Correspondence to Piotr Cyganowski.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Cyganowski, P., Dzimitrowicz, A., Marzec, M.M. et al. Catalytic reductions of nitroaromatic compounds over heterogeneous catalysts with rhenium sub-nanostructures. Sci Rep 13, 12789 (2023). https://doi.org/10.1038/s41598-023-39830-y

Download citation

Received: 15 May 2023

Accepted: 31 July 2023

Published: 07 August 2023

DOI: https://doi.org/10.1038/s41598-023-39830-y

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.